Microstructure of Ni–Al powder and Ni–Al composite coatings prepared by twin-wire arc spraying

Ni–Al powder and Ni–Al composite coatings were fabricated by twin-wire arc spraying (TWAS). The microstructures of Ni-5wt%Al powder and Ni-20wt%Al powder were characterized by scanning electronic microscopy (SEM) and energy dispersive spectroscopy (EDS). The results showed that the obtained particle size ranged from 5 to 50 μm. The morphology of the Ni–Al powder showed that molten particles were composed of Ni solid solution, NiAl, Ni₃Al, Al₂O₃, and NiO. The Ni–Al phase and a small amount of Al₂O₃ particles changed the composition of the coating. The microstructures of the twin-wire-arc-sprayed Ni–Al composite coatings were characterized by SEM, EDS, X-ray diffraction (XRD), and transmission electron microscopy (TEM). The results showed that the main phase of the Ni-5wt%Al coating consisted of Ni solid solution and NiAl in addition to a small amount of Al₂O₃. The main phase of the Ni-20wt%Al coating mainly consisted of Ni solid solution, NiAl, and Ni₃Al in addition to a small amount of Al and Al₂O₃, and NiAl and Ni₃Al intermetallic compounds effectively further improved the final wear property of the coatings. TEM analysis indicated that fine spherical NiAl₃ precipitates and a Ni–Al–O amorphous phase formed in the matrix of the Ni solid solution in the original state.