HOT CORROSION BEHAVIOR OF Ni-BASED SUPERALLOY WITH HIGH Cr CONTENTS -PART 1.EXPERIMENTAL STUDY

+ Author Affiliations
  • Received: 11 June 1996
  • A systematic study of the effects of Ti, Ta and Nb on the hot corrosion behavior of alloy system Ni-16Cr-gAl-2W-1Mo-4Co-(0~4)Ti-(0~4)Ta-(0~4)Nb (at%) was conducted. The results showed that, in certain compositional regions, the hot corrosion resistance in 75% Na2SO4+25%NaCl molten salt of the expermental alloys was similar to that of IN738LC alloy. The hot corrosion property balances with other properties, which provides the basis for selecting alloy compositions to develop single crystal superalloys of high performance hot corrosion resistance.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(281) PDF Downloads(15) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return