Segmented tubular synthesis of monodispersed microsized copper oxalate

Xun Liu; Xing Chen; Kai Huang

doi:10.1007/s12613-019-1753-5

Volume 26 Issue 4

Apr. 2019

Turn off MathJax

数据统计

计量

文章访问数: 555
HTML全文浏览量: 107
PDF下载量: 11
被引次数: 0

文章导航 > 矿物冶金与材料学报（英文） > 2019 > 26(4): 460-466

Xun Liu, Xing Chen, and Kai Huang, Segmented tubular synthesis of monodispersed microsized copper oxalate, Int. J. Miner. Metall. Mater., 26(2019), No. 4, pp. 460-466. https://doi.org/10.1007/s12613-019-1753-5

Cite this article as:

Xun Liu, Xing Chen, and Kai Huang, Segmented tubular synthesis of monodispersed microsized copper oxalate, Int. J. Miner. Metall. Mater., 26(2019), No. 4, pp. 460-466. https://doi.org/10.1007/s12613-019-1753-5

Citation:

PDF( 6086 KB)

引用本文 PDF XML SpringerLink

研究论文

Segmented tubular synthesis of monodispersed microsized copper oxalate

School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
Beijing Key Lab of Green Recycling and Extraction of Metals, University of Science and Technology Beijing, Beijing 100083, China

通讯作者:
Kai Huang E-mail: khuang@metall.ustb.edu.cn

中文摘要

Monodispersed microsized copper oxalate particles were prepared in a segmented continuous flow tube reactor, and the effect of the main parameters such as organic additive agent, initial copper ions concentration, residence time, and segmented media on the final products were investigated experimentally. The obtained copper oxalate microsized particles were disc-like in the presence of citrate ligand, which was the shape inducer for the precipitated copper oxalate. Thermodynamic equilibrium diagrams of the Cu(Ⅱ)-oxalate-H₂O, Cu(Ⅱ)-oxalate-citrate-H₂O, and Cu(Ⅱ)-oxalate-EDTA-H₂O solution systems were drawn to estimate the possible copper species under the experimental conditions and to explain the formation mechanisms of copper oxalate particles in the segmented fluidic reactor. Both theoretical and experimental results indicated that the presence of chelating reagents such as citrate and EDTA had distinct effect on the evolution of particle shape. Air and kerosene were tested as media for the fluidic flow segmentation, and the latter was verified to better promote the growth of copper oxalate particles. The present study provides an easy method to prepare monodispersed copper oxalate microsized particles in a continuous scaling-up way, which can be utilized to prepare the precursor material for conductive inks.

关键词:

Research Article

Segmented tubular synthesis of monodispersed microsized copper oxalate

+ Author Affiliations

Abstract

Abstract

Monodispersed microsized copper oxalate particles were prepared in a segmented continuous flow tube reactor, and the effect of the main parameters such as organic additive agent, initial copper ions concentration, residence time, and segmented media on the final products were investigated experimentally. The obtained copper oxalate microsized particles were disc-like in the presence of citrate ligand, which was the shape inducer for the precipitated copper oxalate. Thermodynamic equilibrium diagrams of the Cu(Ⅱ)-oxalate-H₂O, Cu(Ⅱ)-oxalate-citrate-H₂O, and Cu(Ⅱ)-oxalate-EDTA-H₂O solution systems were drawn to estimate the possible copper species under the experimental conditions and to explain the formation mechanisms of copper oxalate particles in the segmented fluidic reactor. Both theoretical and experimental results indicated that the presence of chelating reagents such as citrate and EDTA had distinct effect on the evolution of particle shape. Air and kerosene were tested as media for the fluidic flow segmentation, and the latter was verified to better promote the growth of copper oxalate particles. The present study provides an easy method to prepare monodispersed copper oxalate microsized particles in a continuous scaling-up way, which can be utilized to prepare the precursor material for conductive inks.
- segmented flow tube reactor;
- copper oxalate powder;
- monodispersed;
- scaling-up;
- shape inducer

FullText(HTML)

Supplements(0)

References(25)

References

[1]	F. Roux, S. Amtablian, M. Anton, et al., Chalcopyrite thin-film solar cells by industry-compatible ink-based process, Sol. Energy Mater. Sol. Cells, 115(2013), p. 86.
[2]	H. Min, B. Lee, S. Jeong, and M. Lee, Fabrication of 10μm-scale conductive Cu patterns by selective laser sintering of Cu complex ink, Opt. Laser Technol., 88(2017), p. 128.
[3]	C.W. Chang, T.Y. Cheng, and Y.C. Liao, Encapsulated silver nanoparticles in water/oil emulsion for conductive inks, J. Taiwan Inst. Chem. Eng., 92(2018), p. 8.
[4]	S. Bose, S. Chakraborty, and D. Sanyal, Water-ethylene glycol mediated synthesis of silver nanoparticles for conductive ink, Mater. Today Proc., 5(2018), No. 3, p. 9941.
[5]	J. Kastner, T. Faury, H.M. Außerhuber, et al., Silver-based reactive ink for inkjet-printing of conductive lines on textiles, Microelectron. Eng., 176(2017), p. 84.
[6]	Z.H. Wang, W. Wang, Z.K. Jiang, and D. Yu, Low temperature sintering nano-silver conductive ink printed on cotton fabric as printed electronics, Prog. Org. Coat., 101(2016), p. 604.
[7]	B.J. De Gans, P.C. Duineveld, and U.S. Schubert, Inkjet printing of polymers:State of the art and future developments, Adv. Mater., 16(2010), No. 3, p. 203.
[8]	D. Kim, S. Jeong, and J. Moon, Synthesis of silver nanoparticles using the polyol process and the influence of precursor injection, Nanotechnology, 17(2006), No. 16, p. 4019.
[9]	T.Öhlund, A.K. Schuppert, M. Hummelgård, J. Bäckström, H.E. Nilsson, and H. Olin, Inkjet fabrication of copper patterns for flexible electronics:Using paper with active precoatings, ACS Appl. Mater. Interfaces, 7(2015), No. 33, p. 18273.
[10]	Y. Hokita, M. Kanzaki, T. Sugiyama, R. Arakawa, and H. Kawasaki, High-concentration synthesis of sub-10 nm copper nanoparticles for application to conductive nanoinks, ACS Appl. Mater. Interfaces, 7(2015), No. 34, p. 19382.
[11]	T. Sugiyama, M. Kanzaki, R. Arakawa, and H. Kawasaki, Low-temperature sintering of metallacyclic stabilized copper nanoparticles and adhesion enhancement of conductive copper film to a polyimide substrate, J. Mater. Sci. Mater. Electron., 27(2016), No. 7, p. 7540.
[12]	A. Yabuki, Y. Tachibana, and I.W. Fathona, Synthesis of copper conductive film by low-temperature thermal decomposition of copper-aminediol complexes under an air atmosphere, Mater. Chem. Phys., 148(2014), No. 1-2, p. 299.
[13]	A. Yabuki, N. Arriffin, and M. Yanase, Low-temperature synthesis of copper conductive film by thermal decomposition of copper-amine complexes, Thin Solid Films, 519(2011), No. 19, p. 6530.
[14]	A. Yabuki and S. Tanaka, Electrically conductive copper film prepared at low temperature by thermal decomposition of copper amine complexes with various amines, Mater. Res. Bull., 47(2012), No. 12, p. 4107.
[15]	D. Adner, F.M. Wolf, S. Möckel, J. Perelaer, U.S. Schubert, and H. Lang, Copper (Ⅱ) ethylene glycol carboxylates as precursors for inkjet printing of conductive copper patterns, Thin Solid Films, 565(2014), p. 143.
[16]	Y. Dong, X.D. Li, S.H. Liu, Q. Zhu, M. Zhang, J.G. Li, and X.D. Sun, Optimizing formulations of silver organic decomposition ink for producing highly-conductive features on flexible substrates:The case study of amines, Thin Solid Films, 616(2016), p. 635.
[17]	A.T. Royappa, A.D. Royappa, R.F. Moral, et al., Copper (I) oxalate complexes:Synthesis, structures and surprises, Polyhedron, 119(2016), p. 563.
[18]	A. Manz, N. Graber, and H.M. Widmer, Miniaturized total chemical analysis systems:A novel concept for chemical sensing, Sens. Actuators B, 1(1990), No. 1-6, p. 244.
[19]	J.H. Chun, S. Lu, Y.S. Lee, and V.W. Pike, Fast and high-yield micro-reactor syntheses of ortho-substituted[¹⁸F]fluoroarenes from reactions of[¹⁸F]fluoride ion with diaryliodonium salts, J. Org. Chem., 75(2010), No. 10, p. 3332.
[20]	S.J. Haswell, R.J. Middleton, B. O'Sullivan, V. Skelton, P. Watts, and P. Styring, ChemInform abstract:The application of micro reactors to synthesis chemistry, Cheminform, 32(2010), No. 23, DOI: 10.1002/chin.200123238.
[21]	K. Schubert, J. Brandner, M. Fichtner, G. Linder, U. Schygulla, and A. Wenka, Microstructure devices for applications in thermal and chemical process engineering, Microscale Thermophys. Eng., 5(2001), No. 1, p. 17.
[22]	K. Jähnisch, V. Hessel, H. Löwe, and M. Baerns, Chemistry in microstructured reactors, Angew. Chem. Int. Ed., 43(2004), No. 4, p. 406.
[23]	M.T. Tang, Theory and Technology of Complex Metallurgy, Central South University Press, Changsha, 2011.
[24]	X.W. Yang and D.F. Qiu, Hydrometallurgy, 2nd Ed., Metallurgical Industry Press, Beijing, 2011.
[25]	X.L. Zhou, Z.G. Yan, and X.D. Han, From ascorbic acid to oxalate:Hydrothermal synthesis of copper oxalate microspheres and conversion to oxide, Mater. Lett., 118(2014), p. 39.

Relative Articles

Cited By

Proportional views

数据统计

姓名
邮箱
手机号码
标题
留言内容
验证码

留言板

数据统计

分享

计量

Segmented tubular synthesis of monodispersed microsized copper oxalate

中文摘要

Segmented tubular synthesis of monodispersed microsized copper oxalate

Abstract

References

数据统计

Catalog