Synthesis and characterization of the nanostructured solid solution with extended solubility of graphite in nickel by mechanical alloying

Nitika Kundan; Biswajit Parida; Anup Kumar Keshri; Prathvi Raj Soni

doi:10.1007/s12613-019-1816-7

Volume 26 Issue 8

Aug. 2019

Turn off MathJax

数据统计

计量

文章访问数: 623
HTML全文浏览量: 162
PDF下载量: 7
被引次数: 0

文章导航 > 矿物冶金与材料学报（英文） > 2019 > 26(8): 1031-1037

Nitika Kundan, Biswajit Parida, Anup Kumar Keshri, and Prathvi Raj Soni, Synthesis and characterization of the nanostructured solid solution with extended solubility of graphite in nickel by mechanical alloying, Int. J. Miner. Metall. Mater., 26(2019), No. 8, pp. 1031-1037. https://doi.org/10.1007/s12613-019-1816-7

Cite this article as:

Nitika Kundan, Biswajit Parida, Anup Kumar Keshri, and Prathvi Raj Soni, Synthesis and characterization of the nanostructured solid solution with extended solubility of graphite in nickel by mechanical alloying, Int. J. Miner. Metall. Mater., 26(2019), No. 8, pp. 1031-1037. https://doi.org/10.1007/s12613-019-1816-7

Citation:

PDF( 2807 KB)

引用本文 PDF XML SpringerLink

研究论文

Synthesis and characterization of the nanostructured solid solution with extended solubility of graphite in nickel by mechanical alloying

Department of Metallurgical and Materials Engineering, Malaviya National Institute of Technology, Jaipur, Rajasthan 302017, India
Department of Materials Science and Engineering, Indian Institute of Technology Patna, Bihar 801106, India

通讯作者:
Prathvi Raj Soni E-mail: prsoni.meta@mnit.ac.in

中文摘要

In the present work, mechanical alloying of a powder mixture of nickel and graphite (up to 15wt%) was carried out in an attrition mill under a nitrogen atmosphere. The as-milled powders were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and transmission electron microscopy (TEM). The 15wt% graphite dissolved into the nickel (exceeding the negligible solid solubility in the nickel-carbon system), thereby forming a supersaturated solid solution of graphite in a nickel matrix. The dissolved graphite occupied interstitial positions along the dislocation edges and at the grain-boundary regions. A three-step graphite dissolution mechanism has been proposed. The associated changes in the nickel lattice, such as changes in the crystallite size (62 to 43 nm), lattice strain (0.12% to 0.3%), and lattice parameter (0.3533 to 0.3586 nm), which led to the formation of the supersaturated solid solution, were also evaluated and discussed.

关键词:

Research Article

Synthesis and characterization of the nanostructured solid solution with extended solubility of graphite in nickel by mechanical alloying

+ Author Affiliations

Abstract

Abstract

In the present work, mechanical alloying of a powder mixture of nickel and graphite (up to 15wt%) was carried out in an attrition mill under a nitrogen atmosphere. The as-milled powders were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and transmission electron microscopy (TEM). The 15wt% graphite dissolved into the nickel (exceeding the negligible solid solubility in the nickel-carbon system), thereby forming a supersaturated solid solution of graphite in a nickel matrix. The dissolved graphite occupied interstitial positions along the dislocation edges and at the grain-boundary regions. A three-step graphite dissolution mechanism has been proposed. The associated changes in the nickel lattice, such as changes in the crystallite size (62 to 43 nm), lattice strain (0.12% to 0.3%), and lattice parameter (0.3533 to 0.3586 nm), which led to the formation of the supersaturated solid solution, were also evaluated and discussed.
- Ni-C system;
- mechanical alloying;
- supersaturated solid solution;
- nanostructured powder

FullText(HTML)

Supplements(0)

References(29)

References

[1]	T. Tanaka, S. Nasu, K.N. Ishihara, and P.H. Shingu, Mechanical alloying of the high carbon Fe-C system, J. Less Common Met., 171(1991), No. 2, p. 237.
[2]	N.Q. Wu, J.M. Wu, G.X. Wang, and Z.Z. Li, Amorphization in the Al-C system by mechanical alloying, J. Alloys Compd., 260(1997), No. 1-2, p. 121.
[3]	H. Arik, Production and characterization of in situ Al₄C₃ reinforced aluminum-based composite produced by mechanical alloying technique, Mater. Des., 25(2004), No. 1, p. 31.
[4]	H.T. Son, T.S. Kim, C. Suryanarayana, and B.S. Chun, Homogeneous dispersion of graphite in a 6061 aluminum alloy by ball milling, Mater. Sci. Eng. A, 348(2003), No. 1-2, p. 163.
[5]	X.R. Liu, Y.B. Liu, X. Ran, J. An, and Z.Y. Cao, Fabrication of the supersaturated solid solution of carbon in copper by mechanical alloying, Mater. Charact., 58(2007), No. 6, p. 504.
[6]	K.N. Ishihara, F. Kubo, E. Yamasue, and H. Okumura, Formation of supersaturated Fe-Li solid solution by mechanical alloying, Rev. Adv. Mater. Sci., 18(2008), No. 3, p. 284.
[7]	B. Ghosh, H. Dutta, and S.K. Pradhan, Microstructure characterization of nanocrystalline Ni₃C synthesized by high-energy ball milling, J. Alloys Compd., 479(2009), No. 1-2, p. 193.
[8]	R.S. Lei, M.P. Wang, H.P. Wang, and S.Q. Xu, New insights on the formation of supersaturated Cu-Nb solid solution prepared by mechanical alloying, Mater. Charact., 118(2016), p. 324.
[9]	Z.Y. Zhong, Z.T. Xiong, L.F. Sun, J.Z. Luo, P. Chen, X. Wu, J. Lin, and K.L. Tan, Nanosized nickel (or cobalt)/graphite composites for hydrogen storage, J. Phys. Chem. B, 106(2002), No. 37, p. 9507.
[10]	J.L. Li and D.S. Xiong, Tribological properties of nickel-based self-lubricating composite at elevated temperature and counterface material selection, Wear, 265(2008), No. 3-4, p. 533.
[11]	I.M. Afanasov, O.N. Shornikova, V.V. Avdeev, O.I. Lebedev, G. Van Tendeloo, and A.T. Matveev, Expanded graphite as a support for Ni/carbon composites, Carbon, 47(2009), No. 2, p. 513.
[12]	C.M. Mani, M. Braun, V. Molinari, M. Antonietti, and N. Fechler, A high-throughput composite catalyst based on nickel carbon cubes for the hydrogenation of 5-hydroxymethylfurfural to 2,5-dimethylfuran, ChemCatChem, 9(2017), No. 17, p. 3388.
[13]	M. Mehrabi, P. Parvin, A. Reyhani, and S.Z. Mortazavi, Hydrogen storage in multi-walled carbon nanotubes decorated with palladium nanoparticles using laser ablation/chemical reduction methods, Mater. Res. Express, 4(2017), No. 9, art. No. 095030.
[14]	R. Akbarzadeh and H. Dehghani, Intensified electrochemical hydrogen storage capacity of multi-walled carbon nanotubes supported with Ni nanoparticles, J. Solid State Electrochem., 22(2018), No. 2, p. 395.
[15]	N. Chawla and K.K. Chawla, Metal Matrix Composite, 2nd ed., Springer New York Heidelberg Dordreche, London, 2013.
[16]	D. Nunes, V. Livramento, R. Mateus, J.B. Correia, L.C. Alves, and M. Vilarigues, Mechanical synthesis of copper-carbon nanocomposites:Structural changes, strengthening and thermal stabilization, Mater. Sci. Eng. A, 528(2011), No. 29-30, p. 8610.
[17]	C. Suryanarayana, Mechanical alloying and milling, Prog. Mater. Sci., 46(2001), No. 1-2, p. 1.
[18]	P.R. Soni, Mechanical Alloying:Fundamentals & Applications, 1st ed., Cambridge International Science Publishing, Cambridge, 2000.
[19]	C.C. Koch, The synthesis and structure of nanocrystalline materials produced by mechanical attrition:A review, Nanostruct. Mater., 2(1993), No. 2, p. 109.
[20]	B. Bokhonov and M. Korchagin, The formation of graphite encapsulated metal nanoparticles during mechanical activation and annealing of soot with iron and nickel, J. Alloys Compd., 333(2002), No. 1-2, p. 308.
[21]	G.L. Caër, E.B. Grosse, A. Pianelli, E. Bouzy, and P. Matteazzi, Mechanically driven syntheses of carbides and silcides, J. Mater. Sci., 25(1990), No. 11, p. 4726.
[22]	T. Tanaka, K.N. Ishihara, and P.H. Shingu, Formation of metastable phases of Ni-C, Metall. Trans. A, 23(1992), No. 9, p. 2431.
[23]	T. Nickchi, M. Ghorbani, A. Alfantazi, and Z. Farhat, Fabrication of low friction bronze-graphite nano-composite coatings, Mater. Des., 32(2011), No. 6, p. 3548.
[24]	T.B. Massalski, H. Okamoto, P.R. Subramanian, and L. Kacprzak, Binary Alloy Phase Diagrams, ASM International, Ohio, 1990, p. 561.
[25]	Badzian and T. Badzian, Growth of diamond and nickel carbide crystals in the Ni-C-H system, Diamond Relat. Mater., 5(1996), No. 1, p. 93.
[26]	B.D. Cullity and S.R. Stock, Elements of X-Ray Diffraction, 3rd ed., Prentice Hall, New Jersy, 2001.
[27]	E. Botcharova, M. Heilmaier, J. Freudenberger, G. Drew, D. Kudashow, U. Martin, and L. Schultza, Supersaturated solid solution of niobium in copper by mechanical alloying, J. Alloys Compd., 351(2003), No. 1-2, p. 119.
[28]	Goyal and P.R. Soni, Functionally graded nanocrystalline silicon powders by mechanical alloying, Mater. Lett., 214(2018), p. 111.
[29]	M.C. Cadeville, C. Lerner, and J.M. Friedt, Electronic structure of interstitial carbon in ferromagnetic transition metals prepared by splat-quenching, Physica B+C, 86-88(1977), p. 432.

Relative Articles

Cited By

Proportional views

数据统计

姓名
邮箱
手机号码
标题
留言内容
验证码

留言板

数据统计

分享

计量

Synthesis and characterization of the nanostructured solid solution with extended solubility of graphite in nickel by mechanical alloying

中文摘要

Synthesis and characterization of the nanostructured solid solution with extended solubility of graphite in nickel by mechanical alloying

Abstract

References

数据统计

Catalog