近 α 耐高温钛合金的显微组织和力学性能在热处理过程中的演变规律

马小昭; 相志磊; 李涛; 陈怡兰; 刘莹莹; 陈子勇; 舒群

doi:10.1007/s12613-021-2248-8

Volume 29 Issue 8

Aug. 2022

Turn off MathJax

图(12) / 表(3)

数据统计

计量

文章访问数: 2493
HTML全文浏览量: 928
PDF下载量: 51
被引次数: 0

文章导航 > 矿物冶金与材料学报（英文） > 2022 > 29(8): 1596-1607

Xiaozhao Ma, Zhilei Xiang, Tao Li, Yilan Chen, Yingying Liu, Ziyong Chen, and Qun Shu, Evolution laws of microstructures and mechanical properties during heat treatments for near-α high-temperature titanium alloys, Int. J. Miner. Metall. Mater., 29(2022), No. 8, pp. 1596-1607. https://doi.org/10.1007/s12613-021-2248-8

Cite this article as:

Xiaozhao Ma, Zhilei Xiang, Tao Li, Yilan Chen, Yingying Liu, Ziyong Chen, and Qun Shu, Evolution laws of microstructures and mechanical properties during heat treatments for near-α high-temperature titanium alloys, Int. J. Miner. Metall. Mater., 29(2022), No. 8, pp. 1596-1607. https://doi.org/10.1007/s12613-021-2248-8

Citation:

PDF( 7246 KB)

引用本文 PDF XML SpringerLink

研究论文

近 α 耐高温钛合金的显微组织和力学性能在热处理过程中的演变规律

1)
北京工业大学材料与制造学部, 北京 100124
2)
国家电网平高集团有限公司, 平顶山 467000
3)
中国航空制造技术研究院, 北京 100024

通讯作者:
陈子勇 E-mail: czy@bjut.edu.cn

中文摘要

耐高温钛合金具有比强度高、比模量高和高温性能优异的优点，主要应用在高性能航空发动机叶片和叶盘，超声速巡航导弹壳体和军用柴油发动机气门等领域。然而，目前对新型耐650℃高温钛合金热处理过程中微纳结构和力学性能演变的研究尚少。本文通过XRD、SEM、EBSD、TEM和拉伸试验等方法研究了热处理过程中合金的显微组织、力学性能和断裂特征的演变规律。研究表明，随固溶温度提升，初生 α 相含量逐渐较小，β 转变组织含量逐渐增加。β 转变组织内部析出大量层片状 α 晶粒，层片的宽度随固溶温度的提升逐渐增加。锻态合金内部既存在尺寸较大的等轴和棒状硅化物，也析出纳米尺寸的硅化物。元素分析表明，大尺寸硅化物或许为(Ti, Zr, Nb)₅Si₃ 和 (Ti, Zr, Nb)₆Si₃。热处理后，尺寸较小的棒状硅化物在残余 β 相中析出，它们与 α/β 界面近似为45°。热处理态合金中的残余 β 相呈半连续状。合金经980°C/1 h固溶和700°C/4 h时效处理后表现出最优的室温和高温（650°C）力学性能的匹配。

关键词:

Research Article

Evolution laws of microstructures and mechanical properties during heat treatments for near-α high-temperature titanium alloys

+ Author Affiliations

Abstract

Abstract

Evolution laws of microstructures, mechanical properties, and fractographs after different solution temperatures were investigated through various analysis methods. With the increasing solution temperatures, contents of the primary α phase decreased, and contents of transformed β structures increased. Lamellar α grains dominated the characteristics of transformed β structures, and widths of secondary α lamellas increased monotonously. For as-forged alloy, large silicides with equiaxed and rod-like morphologies, and nano-scale silicides were found. Silicides with large sizes might be (Ti, Zr, Nb)₅Si₃ and (Ti, Zr, Nb)₆Si₃. Rod-like silicides with small sizes precipitated in retained β phase, exhibiting near 45° angles with α/β boundaries. Retained β phases in as-heat treated alloys were incontinuous. 980STA exhibited an excellent combination of room temperature (RT) and 650°C mechanical properties. Characteristics of fracture surfaces largely depended on the evolutions of microstructures. Meanwhile, silicides promoted the formation of mico-voids.
- solution temperatures;
- microstructures;
- mechanical properties;
- fractographs;
- silicides

FullText(HTML)

Supplements(0)

References(26)

References

[1]	X.J. Jiang, R. Jing, C.Y. Liu, M.Z. Ma, and R.P. Liu, Structure and mechanical properties of TiZr binary alloy after Al addition, Mater. Sci. Eng. A, 586(2013), p. 301. doi: 10.1016/j.msea.2013.08.029
[2]	P. Parvizian, M. Morakabati, and S. Sadeghpour, Effect of hot rolling and annealing temperatures on the microstructure and mechanical properties of SP-700 alloy, Int. J. Miner. Metall. Mater., 27(2020), No. 3, p. 374. doi: 10.1007/s12613-019-1922-6
[3]	J.C. Williams and E.A. Starke Jr, Progress in structural materials for aerospace systems, Acta Mater., 51(2003), No. 19, p. 5775. doi: 10.1016/j.actamat.2003.08.023
[4]	L. Yang, B.Y. Wang, J.G. Lin, H.J. Zhao, and W.Y. Ma, Ductile fracture behavior of TA15 titanium alloy at elevated temperatures, Int. J. Miner. Metall. Mater., 22(2015), No. 10, p. 1082. doi: 10.1007/s12613-015-1171-2
[5]	R. Boyer, G. Welsch, and E. Collings, Materials Properties Handbook: Titanium Alloys, 1994.
[6]	K. Prasad, R. Sarkar, P. Ghosal, D.V.V. Satyanarayana, S.V. Kamat, and T.K. Nandy, Tensile and creep properties of thermomechanically processed boron modified Timetal 834 titanium alloy, Mater. Sci. Eng. A, 528(2011), No. 22-23, p. 6733. doi: 10.1016/j.msea.2011.05.069
[7]	V.K. Chandravanshi, A. Bhattacharjee, S.V. Kamat, and T.K. Nandy, Influence of thermomechanical processing and heat treatment on microstructure, tensile properties and fracture toughness of Ti–1100–0.1B alloy, J. Alloys Compd., 589(2014), p. 336. doi: 10.1016/j.jallcom.2013.11.014
[8]	S.A.A. Shams, S. Mirdamadi, S.M. Abbasi, Y. Lee, and C.S. Lee, Coarsening kinetics of primary alpha in a near alpha titanium alloy, J. Alloys Compd., 735(2018), p. 1769. doi: 10.1016/j.jallcom.2017.11.296
[9]	Q.J. Wang, J.R. Liu, and R. Yang, High temperature titanium alloys: Status and perspective, J. Aeronaut. Mater., 34(2014), No. 4, p. 1. doi: 10.11868/j.issn.1005-5053.2014.4.001
[10]	P.L. Narayana, S.W. Kim, J.K. Hong, N.S. Reddy, and J.T. Yeom, Tensile properties of a newly developed high-temperature titanium alloy at room temperature and 650°C, Mater. Sci. Eng. A, 718(2018), p. 287. doi: 10.1016/j.msea.2018.01.113
[11]	T. Li, L.H. Chai, S.H. Shi, et al., Effect of near-isothermal forging temperature on the microstructure and mechanical properties of near α high temperature titanium alloy, Mater. Sci. Forum, 898(2017), p. 579. doi: 10.4028/www.scientific.net/MSF.898.579
[12]	P. Han, B.L. Li, J.M. Yin, T. Liu, and Z.R. Nie, Effect of Er on creep properties of a near-α high temperature titanium alloy, Sci. Technol. Eng., 12(2012), No. 17, p. 4124.
[13]	X.Z. Ma, L.H. Chai, Y.Y. Liu, et al., TiB whiskers stimulated the dynamic recrystallization behavior, J. Alloys Compd., 812(2020), art. No. 152152. doi: 10.1016/j.jallcom.2019.152152
[14]	Z.B. Zhao, Q.J. Wang, J.R. Liu, and R. Yang, Effect of heat treatment on the crystallographic orientation evolution in a near-α titanium alloy Ti60, Acta Mater., 131(2017), p. 305. doi: 10.1016/j.actamat.2017.04.007
[15]	X.Z. Ma, Z.L. Xiang, M.Z. Ma, Y.P. Cui, W.M. Ren, Z.T. Wang, J.C. Huang, and Z.Y. Chen, Investigation of microstructures, textures, mechanical properties and fracture behaviors of a newly developed near α titanium alloy, Mater. Sci. Eng. A, 775(2020), art. No. 138996. doi: 10.1016/j.msea.2020.138996
[16]	S.X. Liang, M.Z. Ma, R. Jing, X.Y. Zhang, and R.P. Liu, Microstructure and mechanical properties of hot-rolled ZrTiAlV alloys, Mater. Sci. Eng. A, 532(2012), p. 1. doi: 10.1016/j.msea.2011.10.053
[17]	Y. Yue, L.Y. Dai, H. Zhong, C.L. Tan, M.Z. Ma, X.Y. Zhang, and R.P. Liu, Enhanced mechanical properties for mill-annealed Ti–20Zr–6.5Al–4V alloy with a fine equiaxed microstructure, Mater. Sci. Eng. A, 678(2016), p. 286. doi: 10.1016/j.msea.2016.09.116
[18]	S.T. He, W.D. Zeng, J.W. Xu, and W. Chen, The effects of microstructure evolution on the fracture toughness of BT-25 titanium alloy during isothermal forging and subsequent heat treatment, Mater. Sci. Eng. A, 745(2019), p. 203. doi: 10.1016/j.msea.2018.12.062
[19]	J.R. Wood, P.A. Russo, M.F. Welter, and E.M. Crist, Thermomechanical processing and heat treatment of Ti–6Al–2Sn–2Zr–2Cr–2Mo–Si for structural applications, Mater. Sci. Eng. A, 243(1998), No. 1-2, p. 109. doi: 10.1016/S0921-5093(97)00787-9
[20]	J.X. Li, L.Q. Wang, J.N. Qin, Y.F. Chen, W.J. Lu, and D. Zhang, Effect of TRIPLEX heat treatment on tensile properties of in situ synthesized (TiB + La₂O₃)/Ti composite, Mater. Sci. Eng. A, 527(2010), No. 21-22, p. 5811. doi: 10.1016/j.msea.2010.05.065
[21]	S.M.C. van Bohemen, A. Kamp, R.H. Petrov, L.A.I. Kestens, and J. Sietsma, Nucleation and variant selection of secondary α plates in a β Ti alloy, Acta Mater., 56(2008), No. 20, p. 5907. doi: 10.1016/j.actamat.2008.08.016
[22]	S. Mironov, M. Murzinova, S. Zherebtsov, G.A. Salishchev, and S.L. Semiatin, Microstructure evolution during warm working of Ti–6Al–4V with a colony-α microstructure, Acta Mater., 57(2009), No. 8, p. 2470. doi: 10.1016/j.actamat.2009.02.016
[23]	J.X. Li, L.Q. Wang, J.N. Qin, Y.F. Chen, W.J. Lu, and D. Zhang, The effect of heat treatment on thermal stability of Ti matrix composite, J. Alloys Compd., 509(2011), No. 1, p. 52. doi: 10.1016/j.jallcom.2010.09.005
[24]	A.K. Singh, C. Ramachandra, and V. Singh, Orientation relationship between matrix phases and silicide S₂ in alloy Ti–6Al–1.6Zr–3.3Mo–0.3Si, J. Mater. Sci. Lett., 11(1992), No. 4, p. 218. doi: 10.1007/BF00741426
[25]	W.J. Jia, W.D. Zeng, and H.Q. Yu, Effect of aging on the tensile properties and microstructures of a near-alpha titanium alloy, Mater. Des., 58(2014), p. 108. doi: 10.1016/j.matdes.2014.01.063
[26]	C.J. Zhang, X. Li, S.Z. Zhang, L.H. Chai, Z.Y. Chen, F.T. Kong, and Y.Y. Chen, Effects of direct rolling deformation on the microstructure and tensile properties of the 2.5 vol% (TiB_w+TiC_p)/Ti composites, Mater. Sci. Eng. A, 684(2017), p. 645. doi: 10.1016/j.msea.2016.12.113

Relative Articles

Cited By

Proportional views

数据统计

姓名
邮箱
手机号码
标题
留言内容
验证码

留言板

数据统计

分享

计量

近 α 耐高温钛合金的显微组织和力学性能在热处理过程中的演变规律

中文摘要

Evolution laws of microstructures and mechanical properties during heat treatments for near-α high-temperature titanium alloys

Abstract

References

数据统计

Catalog