颗粒微观结构对LiNi0.8Co0.1Mn0.1O2正极材料电性能的影响研究

唐泽勋; 叶红齐; 马鑫; 韩凯

doi:10.1007/s12613-021-2296-0

Volume 29 Issue 8

Aug. 2022

Turn off MathJax

图(8) / 表(4)

数据统计

计量

文章访问数: 794
HTML全文浏览量: 356
PDF下载量: 54
被引次数: 0

文章导航 > 矿物冶金与材料学报（英文） > 2022 > 29(8): 1618-1626

Zexun Tang, Hongqi Ye, Xin Ma, and Kai Han, Effect of particle micro-structure on the electrochemical properties of LiNi_0.8Co_0.1Mn_0.1O₂ cathode material, Int. J. Miner. Metall. Mater., 29(2022), No. 8, pp. 1618-1626. https://doi.org/10.1007/s12613-021-2296-0

Cite this article as:

Zexun Tang, Hongqi Ye, Xin Ma, and Kai Han, Effect of particle micro-structure on the electrochemical properties of LiNi0.8Co0.1Mn0.1O2 cathode material, Int. J. Miner. Metall. Mater., 29(2022), No. 8, pp. 1618-1626. https://doi.org/10.1007/s12613-021-2296-0

Citation:

PDF( 2792 KB)

引用本文 PDF XML SpringerLink

研究论文

颗粒微观结构对LiNi_0.8Co_0.1Mn_0.1O₂正极材料电性能的影响研究

1)
中南大学化学化工学院, 锰资源高效清洁利用湖南省重点实验室, 长沙 410083, 中国
2)
桑顿新能源科技有限公司正极材料研发部, 湘潭 411100, 中国

通讯作者:
马鑫 E-mail: kaihan@csu.edu.cn

韩凯 E-mail: kaihan@csu.edu.cn

文章亮点

(1) 系统地研究了LiNi_0.8Co_0.1Mn_0.1O₂材料二次颗粒与单晶态颗粒的性能差异。

(2) 优化出具有表面低碱度，较高克容量和高温高压循环稳定性的单晶LiNi_0.8Co_0.1Mn_0.1O₂。

(3) 分析了单晶态材料在提高稳定性、降低副反应、抑制循环阻抗上升等方面的作用机理。

中文摘要

锂离子电池正极材料LiNi_0.8Co_0.1Mn_0.1O₂（简称NCM811）能量密度高，有望满足电动汽车长续航里程要求，近年来成为业内关注和研究的焦点。然而，NCM811存在表面碱度高，稳定性差，长循环下颗粒容易碎裂和粉化等问题，阻碍了其大规模应用。本文将三元材料进行单晶化研究，即将二次球颗粒熔融形成单晶颗粒，以期解决三元材料结构和表面稳定性差等问题，并探索在高电压体系使用可行性。实验结果表明，将锂与过渡金属配比设为1.05，在910°C下烧结12 h，可得到形貌较好的单晶NCM811材料，此时材料表面碱度和晶格Ni/Li阳离子混排度均较低，分别为0.288wt%和2.24%。电性能评估结果显示，该材料在3.0–4.3 V下克容量可达191.5mAh/g，同时高温和高电压下循环稳定性得到明显提升，在高温50°C下，3.0–4.4V电压区间内循环100周，容量保持率可达95.1%，而二次颗粒材料仅为88.5%。相比二次颗粒，单晶形态的NCM811材料虽然倍率性能会稍有下降，但结构和表面稳定性更佳，在高电压高能量密度体系具有较好的应用前景。

关键词:

Research Article

Effect of particle micro-structure on the electrochemical properties of LiNi_0.8Co_0.1Mn_0.1O₂ cathode material

+ Author Affiliations

Abstract

Abstract

Ni-rich layered material is a kind of high-capacity cathode to meet the requirement of electric vehicles. As for the typical LiNi_0.8Co_0.1Mn_0.1O₂ material, the particle formation is significant for electrochemical properties of the cathode. In this work, the structure, morphology, and electrochemical performance of LiNi_0.8Co_0.1Mn_0.1O₂ secondary particles and single crystals were systematically studied. A lower Ni²⁺/Ni³⁺ molar ratio of 0.66 and a lower residual alkali content of 0.228wt% were achieved on the surface of the single crystals. In addition, the single crystals showed a discharge capacity of 191.6 mAh/g at 0.2 C (~12 mAh/g lower than that of the secondary particles) and enhanced the electrochemical stability, especially when cycled at 50°C and in a wider electrochemical window (between 3.0 and 4.4 V vs. Li⁺/Li). The LiNi_0.8Co_0.1Mn_0.1O₂ secondary particles were suitable for applications requiring high specific capacity, whereas single crystals exhibited better stability, indicating that they are more suitable for use in long life requested devices.
- Ni-rich layered materials;
- single crystal;
- cathode;
- micro-structure;
- lithium-ion battery

FullText(HTML)

Supplements(0)

References(40)

References

[1]	H.J. Noh, S. Youn, C.S. Yoon, and Y.K. Sun, Comparison of the structural and electrochemical properties of layeredLi[Ni_xCo_yMn_z]O₂ (x = 1/3, 0.5, 0.6, 0.7, 0.8 and 0.85) cathode material for lithium-ion batteries, J. Power Sources, 233(2013), p. 121. doi: 10.1016/j.jpowsour.2013.01.063
[2]	J.B. Goodenough and Y. Kim, Challenges for rechargeable Li batteries, Chem. Mater., 22(2010), No. 3, p. 587. doi: 10.1021/cm901452z
[3]	V. Etacheri, R. Marom, R. Elazari, G. Salitra, and D. Aurbach, Challenges in the development of advanced Li-ion batteries: A review, Energy Environ. Sci., 4(2011), No. 9, p. 3243. doi: 10.1039/c1ee01598b
[4]	Q.W. Ran, H.Y. Zhao, Q. Wang, X.H. Shu, Y.Z. Hu, S. Hao, M. Wang, J.T. Liu, M.L. Zhang, H. Li, N.Y. Liu, and X.Q. Liu, Dual functions of gradient phosphate polyanion doping on improving the electrochemical performance of Ni-rich LiNi_0.6Co_0.2Mn_0.2O₂ cathode at high cut-off voltage and high temperature, Electrochim. Acta, 299(2019), p. 971. doi: 10.1016/j.electacta.2019.01.082
[5]	S.Y. Li, X.L. Fu, Y.W. Liang, S.X. Wang, X.A. Zhou, H. Dong, K.Y. Tuo, C.K. Gao, and X.L. Cui, Enhanced structural stability of boron-doped Layered@Spinel@Carbon heterostructured lithium-rich manganese-based cathode materials, ACS Sustainable Chem. Eng., 8(2020), No. 25, p. 9311. doi: 10.1021/acssuschemeng.0c00870
[6]	L.Z. Deng, F. Wu, X.G. Gao, and W.P. Wu, Development of a LiFePO₄-based high power lithium secondary battery for HEVs applications, Rare Met., 39(2020), No. 12, p. 1457. doi: 10.1007/s12598-014-0316-1
[7]	H.Y. Zhao, X.Y. Gao, Y.F. Li, Q.W. Ran, C.G. Fu, Y.P. Feng, J.T. Liu, X.Q. Liu, and J.X. Su, Synergistic effects of zinc-doping and nano-rod morphology on enhancing the electrochemical properties of spinel Li–Mn–O material, Ceram. Int., 45(2019), No. 14, p. 17591. doi: 10.1016/j.ceramint.2019.05.324
[8]	S. Li, H.Y. Zhou, Z.M. Wang, J.Q. Deng, and Q.R. Yao, Structureand electrochemical properties of La_1−xMg_xNi_2.8Co_0.4Mn_0.1Al_0.2(x = 0.25, 0.30, 0.33) hydrogen storage alloys, Rare Met., 39(2020), No. 12, p. 1464. doi: 10.1007/s12598-014-0322-3
[9]	Q.W. Ran, H.Y. Zhao, X.H. Shu, Y.Z. Hu, S. Hao, Q.Q. Shen, W. Liu, J.T. Liu, M.L. Zhang, H. Li, and X.Q. Liu, Enhancing the electrochemical performance of Ni-rich layered oxide cathodes by combination of the gradient doping and dual-conductive layers coating, ACS Appl. Energy Mater., 2(2019), No. 5, p. 3120. doi: 10.1021/acsaem.8b02112
[10]	N. Nitta, F.X. Wu, J.T. Lee, and G. Yushin, Li-ion battery materials: Present and future, Mater. Today, 18(2015), No. 5, p. 252. doi: 10.1016/j.mattod.2014.10.040
[11]	P.G. Bruce, S.A. Freunberger, L.J. Hardwick, and J.M. Tarascon, Li–O₂ and Li–S batteries with high energy storage, Nat. Mater., 11(2012), No. 1, p. 19. doi: 10.1038/nmat3191
[12]	J.H. Kim, K.J. Park, S.J. Kim, C.S. Yoon, and Y.K. Sun, A method of increasing the energy density of layered Ni-rich Li[Ni_1−2xCo_xMn_x]O₂ cathodes (x = 0.05, 0.1, 0.2), J. Mater. Chem. A, 7(2019), No. 6, p. 2694. doi: 10.1039/C8TA10438G
[13]	C.S. Yoon, M.H. Choi, B.B. Lim, E.J. Lee, and Y.K. Sun, Review–High-capacity Li[Ni_1−xCo_x/2Mn_x/2]O₂ (x = 0.1, 0.05, 0) cathodes for next-generation Li-ion battery, J. Electrochem. Soc., 162(2015), No. 14, p. A2483. doi: 10.1149/2.0101514jes
[14]	Q.W. Ran, H.Y. Zhao, Y.Z. Hu, S. Hao, J.T. Liu, H. Li, and X.Q. Liu, Enhancing surface stability of LiNi_0.8Co_0.1Mn_0.1O₂ cathode with hybrid core-shell nanostructure induced by high-valent titanium ions for Li-ion batteries at high cut-off voltage, J. Alloys Compd., 834(2020), art. No. 155099. doi: 10.1016/j.jallcom.2020.155099
[15]	Q.W. Ran, H.Y. Zhao, Y.Z. Hu, S. Hao, Q.Q. Shen, J.T. Liu, H. Li, Y. Xiao, L. Li, L.P. Wang, and X.Q. Liu, Multifunctional integration of double-shell hybrid nanostructure for alleviating surface degradation of LiNi_0.8Co_0.1Mn_0.1O₂ cathode for advanced lithium-ion batteries at high cutoff voltage, ACS Appl. Mater. Interfaces, 12(2020), No. 8, p. 9268. doi: 10.1021/acsami.9b20872
[16]	W.J. Tang, Z.X. Chen, F. Xiong, F. Chen, C. Huang, Q. Gao, T.Z. Wang, Z.H. Yang, and W.X. Zhang, An effective etching-induced coating strategy to shield LiNi_0.8Co_0.1Mn_0.1O₂ electrode materials by LiAlO₂, J. Power Sources, 412(2019), p. 246. doi: 10.1016/j.jpowsour.2018.11.062
[17]	F. Xiong, Z.X. Chen, C. Huang, T.Z. Wang, W.X. Zhang, Z.H. Yang, and F. Chen, Near-equilibrium control of Li₂TiO₃ nanoscale layer coated on LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials for enhanced electrochemical performance, Inorg. Chem., 58(2019), No. 22, p. 15498. doi: 10.1021/acs.inorgchem.9b02533
[18]	Y. Makimura, T. Sasaki, T. Nonaka, Y.F. Nishimura, T. Uyama, C. Okuda, Y. Itou, and Y. Takeuchi, Factors affecting cycling life of LiNi_0.8Co_0.15Al_0.05O₂ for lithium-ion batteries, J. Mater. Chem. A, 4(2016), No. 21, p. 8350. doi: 10.1039/C6TA01251E
[19]	S.G. Woo, J.H. Kim, H.R. Kim, W. Cho, and J.S. Yu, Failure mechanism analysis of LiNi_0.88Co_0.09Mn_0.03O₂ cathodes in Li-ion full cells, J. Electroanal. Chem., 799(2017), p. 315. doi: 10.1016/j.jelechem.2017.06.034
[20]	A. Iqbal, L. Chen, Y. Chen, Y.X. Gao, F. Chen, and D.C. Li, Lithium-ion full cell with high energy density using nickel-rich LiNi_0.8Co_0.1Mn_0.₁O₂ cathode and SiO–C composite anode, Int. J. Miner. Metall. Mater., 25(2018), No. 12, p. 1473. doi: 10.1007/s12613-018-1702-8
[21]	W.D. Li, H.Y. Asl, Q. Xie, and A. Manthiram, Collapse of LiNi_1–x–yCo_xMn_yO₂ lattice at deep charge irrespective of nickel content in lithium-ion batteries, J. Am. Chem. Soc., 141(2019), No. 13, p. 5097. doi: 10.1021/jacs.8b13798
[22]	J.M. Lim, T. Hwang, D. Kim, M.S. Park, K. Cho, and M. Cho, Intrinsic origins of crack generation in Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ layered oxide cathode material, Sci. Rep., 7(2017), art. No. 39669. doi: 10.1038/srep39669
[23]	A.O. Kondrakov, H. Geßwein, K. Galdina, L. de Biasi, V. Meded, E.O. Filatova, G. Schumacher, W. Wenzel, P. Hartmann, T. Brezesinski, and J. Janek, Charge-transfer-induced lattice collapse in Ni-rich NCM cathode materials during delithiation, J. Phys. Chem. C, 121(2017), No. 44, p. 24381. doi: 10.1021/acs.jpcc.7b06598
[24]	X. Xu, H. Huo, J.Y. Jian, L.G. Wang, H. Zhu, S. Xu, X.S. He, G.P. Yin, C.Y. Du, and X.L. Sun, Radially oriented single-crystal primary nanosheets enable ultrahigh rate and cycling properties of LiNi_0.8Co_0.1Mn_0.1O₂ cathode material for lithium-ion batteries, Adv. Energy Mater., 9(2019), No. 15, art. No. 1803963. doi: 10.1002/aenm.201803963
[25]	J.L. Li, R.M. Yao, and C.B. Cao, LiNi_1/3Co_1/3Mn_1/3O₂ nanoplates with {010} active planes exposing prepared in polyol medium as a high-performance cathode for Li-ion battery, ACS Appl. Mater. Interfaces, 6(2014), No. 7, p. 5075. doi: 10.1021/am500215b
[26]	L. Wang, B.R. Wu, D.B. Mu, X.J. Liu, Y.Y. Peng, H.L. Xu, Q. Liu, L. Gai, and F. Wu, Single-crystal LiNi_0.6Co_0.2Mn_0.2O₂ as high performance cathode materials for Li-ion batteries, J. Alloys Compd., 674(2016), p. 360. doi: 10.1016/j.jallcom.2016.03.061
[27]	Z.D. Huang, X.M. Liu, S.W. Oh, B. Zhang, P.C. Ma, and J.K. Kim, Microscopically porous, interconnected single crystal LiNi_1/3Co_1/3Mn_1/3O₂ cathode material for Lithium ion batteries, J. Mater. Chem., 21(2011), No. 29, p. 10777. doi: 10.1039/c1jm00059d
[28]	B.L. Ellis, K.T. Lee, and L.F. Nazar, Positive electrode materials for Li-ion and Li-batteries, Chem. Mater., 22(2010), No. 3, p. 691. doi: 10.1021/cm902696j
[29]	S. Xu, C.Y. Du, X. Xu, G.K. Han, P.J. Zuo, X.Q. Cheng, Y.L. Ma, and G.P. Yin, A mild surface washing method using protonated polyaniline for Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ material of lithium ion batteries, Electrochim. Acta, 248(2017), p. 534. doi: 10.1016/j.electacta.2017.07.169
[30]	K. Qian, B.H. Huang, Y.X. Liu, M. Wagemaker, M. Liu, H. Duan, D.Q. Liu, Y.B. He, B.H. Li, and F.Y. Kang, Increase and discretization of the energy barrier for individual LiNi_xCo_yMn_yO₂(x + 2y = 1) particles with the growth of a Li₂CO₃ surface film, J. Mater. Chem. A, 7(2019), No. 20, p. 12723. doi: 10.1039/C9TA01443H
[31]	L.W. Liang, G.R. Hu, F. Jiang, and Y.B. Cao, Electrochemical behaviours of SiO₂-coated LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials by a novel modification method, J. Alloys Compd., 657(2016), p. 570. doi: 10.1016/j.jallcom.2015.10.177
[32]	T. Chen, X. Li, H. Wang, X.X. Yan, L. Wang, B.W. Deng, W.J. Ge, and M.Z. Qu, The effect of gradient boracic polyanion-doping on structure, morphology, and cycling performance of Ni-rich LiNi_0.8Co_0.15Al_0.05O₂ cathode material, J. Power Sources, 374(2018), p. 1. doi: 10.1016/j.jpowsour.2017.11.020
[33]	B.H. Toby, EXPGUI, a graphical user interface for GSAS, J. Appl. Crystallogr., 34(2001), No. 2, p. 210. doi: 10.1107/S0021889801002242
[34]	H.B. Lin, Y.M. Zhang, H.B. Rong, S.W. Mai, J.N. Hu, Y.H. Liao, L.D. Xing, M.Q. Xu, X.P. Li, and W.S. Li, Crystallographic facet- and size-controllable synthesis of spinel LiNi_0.5Mn_1.5O₄ with excellent cyclic stability as cathode of high voltage lithium ion battery, J. Mater. Chem. A, 2(2014), No. 30, p. 11987. doi: 10.1039/C4TA01810A
[35]	Y.J. Bi, W.C. Yang, R. Du, J.J. Zhou, M. Liu, Y. Liu, and D.Y. Wang, Correlation of oxygen non-stoichiometry to the instabilities and electrochemical performance of LiNi_0.8Co_0.1Mn_0.1O₂ utilized in lithium ion battery, J. Power Sources, 283(2015), p. 211. doi: 10.1016/j.jpowsour.2015.02.095
[36]	N.T. Wu, H. Wu, J.K. Kim, X.M. Liu, and Y. Zhang, Restoration of degraded nickel-rich cathode materials for long-life lithium-ion batteries, ChemElectroChem, 5(2018), No. 1, p. 78. doi: 10.1002/celc.201700979
[37]	S. Gao, Y.T. Cheng, and M. Shirpour, Effects of cobalt deficiency on nickel-rich layered LiNi_0.8Co_0.1Mn_0.1O₂ positive electrode materials for lithium-ion batteries, ACS Appl. Mater. Interfaces, 11(2019), No. 1, p. 982. doi: 10.1021/acsami.8b19349
[38]	W. Liu, P. Oh, X.E. Liu, M.J. Lee, W. Cho, S. Chae, Y. Kim, and J. Cho, Nickel-rich layered lithium transition-metal oxide for high-energy lithium-ion batteries, Angew. Chem. Int. Ed., 54(2015), No. 15, p. 4440. doi: 10.1002/anie.201409262
[39]	J.X. Zheng, Y.K. Ye, T.C. Liu, Y.G. Xiao, C.M. Wang, F. Wang, and F. Pan, Ni/Li disordering in layered transition metal oxide: Electrochemical impact, origin, and control, Acc. Chem. Res., 52(2019), No. 8, p. 2201. doi: 10.1021/acs.accounts.9b00033
[40]	E.Y. Zhao, M.M. Chen, Z.B. Hu, D.F. Chen, L.M. Yang, and X.L. Xiao, Improved cycle stability of high-capacity Ni-rich LiNi_0.8Mn_0.1Co_0.1O₂ at high cut-off voltage by Li₂SiO₃ coating, J. Power Sources, 343(2017), p. 345. doi: 10.1016/j.jpowsour.2017.01.066