FeCoNiCrMo高熵纳米片催化改善氢化镁的固态储氢性能

钟涛; 章浩宇; 宋梦臣; 蒋艺群; 商丹红; 吴富英; 张刘挺

doi:10.1007/s12613-023-2669-7

Volume 30 Issue 11

Nov. 2023

Turn off MathJax

图(8) / 表(1)

数据统计

计量

文章访问数: 1284
HTML全文浏览量: 248
PDF下载量: 41
被引次数: 0

文章导航 > 矿物冶金与材料学报（英文） > 2023 > 30(11): 2270-2279

Tao Zhong, Haoyu Zhang, Mengchen Song, Yiqun Jiang, Danhong Shang, Fuying Wu, and Liuting Zhang, FeCoNiCrMo high entropy alloy nanosheets catalyzed magnesium hydride for solid-state hydrogen storage, Int. J. Miner. Metall. Mater., 30(2023), No. 11, pp. 2270-2279. https://doi.org/10.1007/s12613-023-2669-7

Cite this article as:

Tao Zhong, Haoyu Zhang, Mengchen Song, Yiqun Jiang, Danhong Shang, Fuying Wu, and Liuting Zhang, FeCoNiCrMo high entropy alloy nanosheets catalyzed magnesium hydride for solid-state hydrogen storage, Int. J. Miner. Metall. Mater., 30(2023), No. 11, pp. 2270-2279. https://doi.org/10.1007/s12613-023-2669-7

Citation:

PDF( 3269 KB)

引用本文 PDF XML SpringerLink

研究论文

FeCoNiCrMo高熵纳米片催化改善氢化镁的固态储氢性能

1)
江苏科技大学能源与动力学院, 分析测试中心, 镇江 212003, 中国
2)
Max Planck Institute for Iron Research, Düsseldorf, 40237, Germany
3)
江苏科技大学环境与化学工程学院, 镇江 212003, 中国

通讯作者:
吴富英 E-mail: wufuying@just.edu.cn

张刘挺 E-mail: zhanglt89@just.edu.cn

文章亮点

(1) 通过湿化学球磨制备了FeCoNiCrMo高熵合金纳米片。

(2) 首次将高熵合金FeCoNiCrMo纳米引入到MgH₂体系中，较好的改进了其储氢性能。

(3) Fe、Co、Ni、Cr和Mo五种元素的协同催化作用，有助于MgH₂中氢的快速转移。

中文摘要

作为一种高密度（7.6wt%，110 kg·m⁻³）固态储氢材料，氢化镁（MgH₂）在氢气运输和储存方面大有可为。然而，其稳定的热力学特性和缓慢的动力学特性限制了其实际应用。在各种被采用的改性方法中，催化掺杂被证实在调整MgH₂放氢和吸氢性能方面发挥着重要作用。本文首次研究了铁钴镍铬钼高熵合金纳米片对MgH₂储氢性能的催化作用。实验结果表明，掺杂了9wt% FeCoNiCrMo的MgH₂在200°C开始脱氢，并在325°C下60分钟内释放出5.89wt%的氢。完全脱氢的复合材料可在低至100°C的温度下于50分钟内吸收3.23wt%的氢气。与MgH₂相比，复合材料的脱氢 ((84.47 ± 1.09) kJ·mol⁻¹）和加氢((33.02 ± 0.10) kJ·mol⁻¹)活化能分别比MgH₂降低了44.21%和55.22%。此外，复合材料的氢容量在20次循环后仅下降了0.28wt%，显示出良好的循环稳定性。微观结构分析证实，在循环过程中，Fe、Co、Ni、Cr和Mo五种元素以高熵合金的形式稳定存在，五种元素协同催化促进了MgH₂的脱氢/加氢反应。此外，FeCoNiCrMo和MgH₂之间的紧密接触提供了大量的异质活化位点和扩散通道，有助于MgH₂–9wt% FeCoNiCrMo复合材料中氢的快速转移。

关键词:

Research Article

FeCoNiCrMo high entropy alloy nanosheets catalyzed magnesium hydride for solid-state hydrogen storage

+ Author Affiliations

1)
School of Energy and Power, Instrumental Analysis Center, Jiangsu University of Science and Technology, Zhenjiang 212003, China
2)
Max Planck Institute for Iron Research, Düsseldorf, 40237, Germany
3)
School of Environmental and Chemical Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003, China

Liuting Zhang is a youth editorial board member for this journal and was not involved in the editorial review or the decision to publish this article. The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

Corresponding authors:
Fuying Wu E-mail: wufuying@just.edu.cn

Liuting Zhang E-mail: zhanglt89@just.edu.cn
Received: 25 February 2023; Revised: 13 April 2023; Accepted: 4 May 2023; Available online: 6 May 2023

Abstract

Abstract

The catalytic effect of FeCoNiCrMo high entropy alloy nanosheets on the hydrogen storage performance of magnesium hydride (MgH₂) was investigated for the first time in this paper. Experimental results demonstrated that 9wt% FeCoNiCrMo doped MgH₂ started to dehydrogenate at 200°C and discharged up to 5.89wt% hydrogen within 60 min at 325°C. The fully dehydrogenated composite could absorb 3.23wt% hydrogen in 50 min at a temperature as low as 100°C. The calculated de/hydrogenation activation energy values decreased by 44.21%/55.22% compared with MgH₂, respectively. Moreover, the composite’s hydrogen capacity dropped only 0.28wt% after 20 cycles, demonstrating remarkable cycling stability. The microstructure analysis verified that the five elements, Fe, Co, Ni, Cr, and Mo, remained stable in the form of high entropy alloy during the cycling process, and synergistically serving as a catalytic union to boost the de/hydrogenation reactions of MgH₂. Besides, the FeCoNiCrMo nanosheets had close contact with MgH₂, providing numerous non-homogeneous activation sites and diffusion channels for the rapid transfer of hydrogen, thus obtaining a superior catalytic effect.
- hydrogen storage;
- magnesium hydride;
- high entropy alloy;
- nano-sheets;
- catalysis

FullText(HTML)

Supplements(0)

References(55)

References

[1]	T.Z. Wang, X.J. Cao, and L.F. Jiao, Ni₂P/NiMoP heterostructure as a bifunctional electrocatalyst for energy-saving hydrogen production, eScience, 1(2021), No. 1, p. 69. doi: 10.1016/j.esci.2021.09.002
[2]	M.C. Song, L.T. Zhang, F.Y. Wu, et al., Recent advances of magnesium hydride as an energy storage material, J. Mater. Sci. Technol., 149(2023), p. 99. doi: 10.1016/j.jmst.2022.11.032
[3]	Z.Q. Lan, H.R. Liang, X.B. Wen, et al., Experimental and theoretical studies on two-dimensional vanadium carbide hybrid nanomaterials derived from V₄AlC₃ as excellent catalyst for MgH₂, J. Magnes. Alloys, (2022). https://doi.org/10.1016/j.jma.2022.09.019
[4]	Y.X. Jia, X.C. Wang, L.J. Hu, et al., Carbon composite support improving catalytic effect of NbC nanoparticles on the low-temperature hydrogen storage performance of MgH₂, J. Mater. Sci. Technol., 150(2023), p. 65. doi: 10.1016/j.jmst.2022.11.044
[5]	L. Zang, W.Y. Sun, S. Liu, et al., Enhanced hydrogen storage properties and reversibility of LiBH₄ confined in two-dimensional Ti₃C₂, ACS Appl. Mater. Interfaces, 10(2018), No. 23, p. 19598. doi: 10.1021/acsami.8b02327
[6]	N.A. Sazelee and M. Ismail, Recent advances in catalyst-enhanced LiAlH₄ for solid-state hydrogen storage: A review, Int. J. Hydrogen Energy, 46(2021), No. 13, p. 9123. doi: 10.1016/j.ijhydene.2020.12.208
[7]	T. Wang and K.F. Aguey-Zinsou, Controlling the growth of NaBH₄ nanoparticles for hydrogen storage, Int. J. Hydrogen Energy, 45(2020), No. 3, p. 2054. doi: 10.1016/j.ijhydene.2019.11.061
[8]	Q. Luo, J.D. Li, B. Li, B. Liu, H.Y. Shao, and Q. Li, Kinetics in Mg-based hydrogen storage materials: Enhancement and mechanism, J. Magnes. Alloys, 7(2019), No. 1, p. 58. doi: 10.1016/j.jma.2018.12.001
[9]	Q. Luo, Y.L. Guo, B. Liu, et al., Thermodynamics and kinetics of phase transformation in rare earth–magnesium alloys: A critical review, J. Mater. Sci. Technol., 44(2020), p. 171. doi: 10.1016/j.jmst.2020.01.022
[10]	S. Guemou, D.Q. Gao, F.Y. Wu, et al., Enhanced hydrogen storage kinetics of MgH₂ by the synergistic effect of Mn₃O₄/ZrO₂ nanoparticles, Dalton Trans., 52(2023), No. 3, p. 609. doi: 10.1039/D2DT03769F
[11]	S.M. Zhou, D. Wei, H.Y. Wan, et al., Efficient catalytic effect of the page-like MnCo₂O_4.5 catalyst on the hydrogen storage performance of MgH₂, Inorg. Chem. Front., 9(2022), No. 21, p. 5495. doi: 10.1039/D2QI01715F
[12]	X.L. Zhang, Y.F. Liu, X. Zhang, J.J. Hu, M.X. Gao, and H.G. Pan, Empowering hydrogen storage performance of MgH₂ by nanoengineering and nanocatalysis, Mater. Today Nano, 9(2020), art. No. 100064. doi: 10.1016/j.mtnano.2019.100064
[13]	Z. Ding, Y.T. Li, H. Yang, et al., Tailoring MgH₂ for hydrogen storage through nanoengineering and catalysis, J. Magnes. Alloys, 10(2022), No. 11, p. 2946. doi: 10.1016/j.jma.2022.09.028
[14]	R.B. Strozi, D.R. Leiva, J. Huot, W.J. Botta, and G. Zepon, Synthesis and hydrogen storage behavior of Mg–V–Al–Cr–Ni high entropy alloys, Int. J. Hydrogen Energy, 46(2021), No. 2, p. 2351. doi: 10.1016/j.ijhydene.2020.10.106
[15]	J. Cermak, L. Kral, and P. Roupcova, Hydrogen storage in TiVCrMo and TiZrNbHf multiprinciple-element alloys and their catalytic effect upon hydrogen storage in Mg, Renew. Energy, 188(2022), p. 411. doi: 10.1016/j.renene.2022.02.021
[16]	A. Grill, J. Horky, A. Panigrahi, G. Krexner, and M. Zehetbauer, Long-term hydrogen storage in Mg and ZK60 after Severe Plastic Deformation, Int. J. Hydrogen Energy, 40(2015), No. 47, p. 17144. doi: 10.1016/j.ijhydene.2015.05.145
[17]	J.J. Márquez, J. Soyama, R.D.A. Silva, et al., Processing of MgH₂ by extensive cold rolling under protective atmosphere, Int. J. Hydrogen Energy, 42(2017), No. 4, p. 2201. doi: 10.1016/j.ijhydene.2016.10.056
[18]	Y. Zhong, X.F. Wan, Z. Ding, and L.L. Shaw, New dehydrogenation pathway of LiBH₄ + MgH₂ mixtures enabled by nanoscale LiBH₄, Int. J. Hydrogen Energy, 41(2016), No. 47, p. 22104. doi: 10.1016/j.ijhydene.2016.09.195
[19]	G. Mulas, R. Campesi, S. Garroni, et al., Hydrogen storage in 2NaBH₄ + MgH₂ mixtures: Destabilization by additives and nanoconfinement, J. Alloys Compd., 536(2012), Suppl. 1, p. S236.
[20]	Z.Y. Lu, J.H. He, M.C. Song, et al., Bullet-like vanadium-based MOFs as a highly active catalyst for promoting the hydrogen storage property in MgH₂, Int. J. Miner. Metall. Mater., 30(2023), No. 1, p. 44. doi: 10.1007/s12613-021-2372-5
[21]	Z.Y. Lu, H.J. Yu, X. Lu, et al., Two-dimensional vanadium nanosheets as a remarkably effective catalyst for hydrogen storage in MgH₂, Rare Met., 40(2021), No. 11, p. 3195. doi: 10.1007/s12598-021-01764-7
[22]	N. Sazelee, M.F.M. Din, and M. Ismail, Ni_0.6Zn_0.4O synthesised via a solid-state method for promoting hydrogen sorption from MgH₂, Materials, 16(2023), No. 6, art. No. 2176. doi: 10.3390/ma16062176
[23]	X.Q. Duan, G.X. Li, W.H. Zhang, et al., Ti₃AlCN MAX for tailoring MgH₂ hydrogen storage material: From performance to mechanism, Rare Met., 42(2023), No. 6, p. 1923. doi: 10.1007/s12598-022-02231-7
[24]	G.B. Tian, F.Y. Wu, H.Y. Zhang, J. Wei, H. Zhao, and L.T. Zhang, Boosting the hydrogen storage performance of MgH₂ by Vanadium based complex oxides, J. Phys. Chem. Solids, 174(2023), art. No. 111187. doi: 10.1016/j.jpcs.2022.111187
[25]	M.M. Jiang, J. Xu, P. Munroe, and Z.H. Xie, First-principles study on the hydrogen storage properties of MgH₂(101) surface by CuNi co-doping, Chem. Phys., 565(2023), art. No. 111760. doi: 10.1016/j.chemphys.2022.111760
[26]	S.A. Pighin, G. Capurso, S.L. Russo, and H.A. Peretti, Hydrogen sorption kinetics of magnesium hydride enhanced by the addition of Zr₈Ni₂₁ alloy, J. Alloys Compd., 530(2012), p. 111. doi: 10.1016/j.jallcom.2012.03.100
[27]	X. Lu, L.T. Zhang, H.J. Yu, et al., Achieving superior hydrogen storage properties of MgH₂ by the effect of TiFe and carbon nanotubes, Chem. Eng. J., 422(2021), art. No. 130101. doi: 10.1016/j.cej.2021.130101
[28]	Y.Y. Zhao, Y.F. Zhu, J.C. Liu, et al., Enhancing hydrogen storage properties of MgH₂ by core-shell CoNi@C, J. Alloys Compd., 862(2021), art. No. 158004. doi: 10.1016/j.jallcom.2020.158004
[29]	S. Singh, A. Bhatnagar, V. Shukla, et al., Ternary transition metal alloy FeCoNi nanoparticles on graphene as new catalyst for hydrogen sorption in MgH₂, Int. J. Hydrogen Energy, 45(2020), No. 1, p. 774. doi: 10.1016/j.ijhydene.2019.10.204
[30]	A.G. Manjón, T. Löffler, M. Meischein, et al., Sputter deposition of highly active complex solid solution electrocatalysts into an ionic liquid library: Effect of structure and composition on oxygen reduction activity, Nanoscale, 12(2020), No. 46, p. 23570. doi: 10.1039/D0NR07632E
[31]	D.S. Wu, K. Kusada, T. Yamamoto, et al., On the electronic structure and hydrogen evolution reaction activity of platinum group metal-based high-entropy-alloy nanoparticles, Chem. Sci., 11(2020), No. 47, p. 12731. doi: 10.1039/D0SC02351E
[32]	H.J. Qiu, G. Fang, J.J. Gao, et al., Noble metal-free nanoporous high-entropy alloys as high efficient electrocatalysts for oxygen evolution reaction, ACS Materials Lett., 1(2019), No. 5, p. 526. doi: 10.1021/acsmaterialslett.9b00414
[33]	Y.G. Yao, Z.Y. Liu, P.F. Xie, et al., Computationally aided, entropy-driven synthesis of highly efficient and durable multi-elemental alloy catalysts, Sci. Adv., 6(2020), No. 11, art. No. eaaz0510. doi: 10.1126/sciadv.aaz0510
[34]	P. Meena, R. Singh, V.K. Sharma, and I.P. Jain, Role of NiMn_9.3Al_4.0Co_14.1Fe_3.6 alloy on dehydrogenation kinetics of MgH₂, J. Magnes. Alloys, 6(2018), No. 3, p. 318. doi: 10.1016/j.jma.2018.05.007
[35]	M.S. El-Eskandarany, S.A. Ahmed, and E. Shaban, Metallic glassy V₄₅Zr₂₀Ni₂₀Cu₁₀Al₃Pd₂ alloy powders for superior hydrogenation/dehydrogenation kinetics of MgH₂, Mater. Today, 5(2018), No. 5, p. 13718. doi: 10.1016/j.matpr.2018.02.010
[36]	P. Edalati, R. Floriano, A. Mohammadi, et al., Reversible room temperature hydrogen storage in high-entropy alloy TiZrCrMnFeNi, Scripta Mater., 178(2020), p. 387. doi: 10.1016/j.scriptamat.2019.12.009
[37]	R. Floriano, G. Zepon, K. Edalati, et al., Hydrogen storage in TiZrNbFeNi high entropy alloys, designed by thermodynamic calculations, Int. J. Hydrogen Energy, 45(2020), No. 58, p. 33759. doi: 10.1016/j.ijhydene.2020.09.047
[38]	R. Floriano, G. Zepon, K. Edalati, et al., Hydrogen storage properties of new A₃B₂-type TiZrNbCrFe high-entropy alloy, Int. J. Hydrogen Energy, 46(2021), No. 46, p. 23757. doi: 10.1016/j.ijhydene.2021.04.181
[39]	A. Mohammadi, Y. Ikeda, P. Edalati, et al., High-entropy hydrides for fast and reversible hydrogen storage at room temperature: Binding-energy engineering via first-principles calculations and experiments, Acta Mater., 236(2022), art. No. 118117. doi: 10.1016/j.actamat.2022.118117
[40]	R.V. Muraleedharan, On Johnson-Mehl-Avrami equation, J. Therm. Anal., 37(1991), No. 11, p. 2729.
[41]	E. Xu, H. Li, X.M. You, et al., Influence of micro-amount O₂ or N₂ on the hydrogenation/dehydrogenation kinetics of hydrogen-storage material MgH₂, Int. J. Hydrogen Energy, 42(2017), No. 12, p. 8057. doi: 10.1016/j.ijhydene.2016.12.102
[42]	M. Ismail, M.S. Yahya, N.A. Sazelee, N.A. Ali, F.A.H. Yap, and N.S. Mustafa, The effect of K₂SiF₆ on the MgH₂ hydrogen storage properties, J. Magnes. Alloys, 8(2020), No. 3, p. 832. doi: 10.1016/j.jma.2020.04.002
[43]	M.S. El-Eskandarany, E. Shaban, H. Al-Matrouk, et al., Structure, morphology and hydrogen storage kinetics of nanocomposite MgH₂/10wt% ZrNi₅ powders, Mater. Today Energy, 3(2017), p. 60. doi: 10.1016/j.mtener.2016.12.002
[44]	M.S. Yahya and M. Ismail, Catalytic effect of SrTiO₃ on the hydrogen storage behaviour of MgH₂, J. Energy Chem., 28(2019), p. 46. doi: 10.1016/j.jechem.2017.10.020
[45]	J.Q. Zhang, Q.H. Hou, X.T. Guo, and X.L. Yang, Achieve high-efficiency hydrogen storage of MgH₂ catalyzed by nanosheets CoMoO₄ and rGO, J. Alloys Compd., 911(2022), art. No. 165153. doi: 10.1016/j.jallcom.2022.165153
[46]	C.S. Zhou, R.C. Bowman Jr., Z.Z. Fang, et al., Amorphous TiCu-based additives for improving hydrogen storage properties of magnesium hydride, ACS Appl. Mater. Interfaces, 11(2019), No. 42, p. 38868. doi: 10.1021/acsami.9b16076
[47]	M.S. Yahya, N.N. Sulaiman, N.S. Mustafa, F.A.H. Yap, and M. Ismail, Improvement of hydrogen storage properties in MgH₂ catalysed by K₂NbF₇, Int. J. Hydrogen Energy, 43(2018), No. 31, p. 14532. doi: 10.1016/j.ijhydene.2018.05.157
[48]	M.S. El-Eskandarany, F. Al-Ajmi, and M. Banyan, Mechanically-induced catalyzation of MgH₂ powders with Zr₂Ni-ball milling media, Catalysts, 9(2019), No. 4, art. No. 382. doi: 10.3390/catal9040382
[49]	L.T. Zhang, Z.L. Cai, X.Q. Zhu, et al., Two-dimensional ZrCo nanosheets as highly effective catalyst for hydrogen storage in MgH₂, J. Alloys Compd., 805(2019), p. 295. doi: 10.1016/j.jallcom.2019.07.085
[50]	M.C. Song, L.T. Zhang, Z.D. Yao, et al., Unraveling the degradation mechanism for the hydrogen storage property of Fe nanocatalyst-modified MgH₂, Inorg. Chem. Front., 9(2022), No. 15, p. 3874. doi: 10.1039/D2QI00863G
[51]	L.T. Zhang, H.J. Yu, Z.Y. Lu, et al., The effect of different Co phase structure (FCC/HCP) on the catalytic action towards the hydrogen storage performance of MgH₂, Chin. J. Chem. Eng., 43(2022), p. 343. doi: 10.1016/j.cjche.2021.10.016
[52]	N. Xu, Z.R. Yuan, Z.H. Ma, et al., Effects of highly dispersed Ni nanoparticles on the hydrogen storage performance of MgH₂, Int. J. Miner. Metall. Mater., 30(2023), No. 1, p. 54. doi: 10.1007/s12613-022-2510-8
[53]	J. Bystrzycki, T. Czujko, and R.A. Varin, Processing by controlled mechanical milling of nanocomposite powders Mg + X (X = Co, Cr, Mo, V, Y, Zr) and their hydrogenation properties, J. Alloys Compd., 404-406(2005), p. 507. doi: 10.1016/j.jallcom.2004.10.094
[54]	Z.Y. Han, S.X. Zhou, H.P. Chen, H.L. Niu, and N.F. Wang, Enhancement of the hydrogen storage properties of Mg/C nanocomposites prepared by reactive milling with molybdenum, J. Wuhan Univ. Technol. Mater. Sci. Ed., 32(2017), No. 2, p. 299. doi: 10.1007/s11595-017-1596-8
[55]	N.K. Katiyar, K. Biswas, J.W. Yeh, S. Sharma, and C.S. Tiwary, A perspective on the catalysis using the high entropy alloys, Nano Energy, 88(2021), art. No. 106261. doi: 10.1016/j.nanoen.2021.106261