低成本钠离子电池玻璃纤维隔膜的高效利用

马小航; 陈志杰; 张天文; 张雪倩; 马元; 郭雁青; 魏义永; 葛梦缘; 候之国; 訾振发

doi:10.1007/s12613-023-2691-9

Volume 30 Issue 10

Oct. 2023

Turn off MathJax

图(9) / 表(1)

数据统计

计量

文章访问数: 959
HTML全文浏览量: 334
PDF下载量: 73
被引次数: 0

文章导航 > 矿物冶金与材料学报（英文） > 2023 > 30(10): 1878-1886

Xiaohang Ma, Zhijie Chen, Tianwen Zhang, Xueqian Zhang, Yuan Ma, Yanqing Guo, Yiyong Wei, Mengyuan Ge, Zhiguo Hou, and Zhenfa Zi, Efficient utilization of glass fiber separator for low-cost sodium-ion batteries, Int. J. Miner. Metall. Mater., 30(2023), No. 10, pp. 1878-1886. https://doi.org/10.1007/s12613-023-2691-9

Cite this article as:

Xiaohang Ma, Zhijie Chen, Tianwen Zhang, Xueqian Zhang, Yuan Ma, Yanqing Guo, Yiyong Wei, Mengyuan Ge, Zhiguo Hou, and Zhenfa Zi, Efficient utilization of glass fiber separator for low-cost sodium-ion batteries, Int. J. Miner. Metall. Mater., 30(2023), No. 10, pp. 1878-1886. https://doi.org/10.1007/s12613-023-2691-9

Citation:

PDF( 3947 KB)

引用本文 PDF XML SpringerLink

研究论文

低成本钠离子电池玻璃纤维隔膜的高效利用

1)
合肥师范学院物理与材料工程学院, 合肥 230601, 中国
2)
中国科学技术大学化学与材料科学学院, 合肥 230026, 中国

通讯作者:
訾振发 E-mail: zfzi@issp.ac.cn

文章亮点

(1) 提出了利用低成本、高韧性的滤纸复合改性高成本、低强度的玻璃纤维的设计思路。

(2) 开发了一种简单的流浆过筛工艺用以制备新型复合隔膜。

(3) 系统研究了滤纸与玻璃纤维不同复合比例对制备隔膜性能的影响。

中文摘要

隔膜是钠离子电池的关键组成部分，其性能极大影响着钠离子电池的电化学性能和安全特性。常规使用的玻璃纤维滤纸因高成本和差的机械性能而不能满足钠离子电池大规模应用的要求。本文以玻璃纤维隔膜边角料和普通定性滤纸为原料，通过简单的流浆过筛工艺制备出了一系列新型复合隔膜。当玻璃纤维与滤纸复合质量比例为1:1时，复合隔膜获得了优异的综合性能，其拉伸强度达到15.8 MPa，孔隙率为74.3%，离子电导率为1.57 × 10⁻³ S·cm⁻¹，并且该隔膜可在210°C保持良好的尺寸稳定性。组装的钠离子电池同样显示出了良好的循环性能（1C下500次循环后容量保持率为94.1%）和倍率性能（10C下放电比容量保持率为87.3%），并与电极保持了良好的界面稳定性。以上结果为高性能、低成本钠离子电池的隔膜设计提供了一些新思路。

关键词:

Research Article

Efficient utilization of glass fiber separator for low-cost sodium-ion batteries

+ Author Affiliations

Abstract

Abstract

The separator is a key component of sodium-ion battery, which greatly affects the electrochemical performances and safety characteristics of the battery. Conventional glass fiber separator cannot meet the requirements of large-scale application because of high cost and poor mechanical properties. Herein, the novel composite separators are prepared by a simple slurry sieving process using glass fiber separator scraps and ordinary qualitative filter paper as raw materials. As the composite mass ratio is 1:1, the composite separator has excellent comprehensive properties, including tensile strength of 15.8 MPa, porosity of 74.3%, ionic conductivity of 1.57 × 10⁻³ S·cm⁻¹ and thermal stability at 210°C. The assembled sodium-ion battery shows superior cycling performance (capacity retention of 94.1% after 500 cycles at 1C) and rate capacity (retention rate of 87.3% at 10C), and it maintains fine interface stability. The above results provide some new ideas for the separator design of high-performance and low-cost sodium-ion batteries.
- separator;
- glass fiber;
- low cost;
- sodium-ion batteries

FullText(HTML)

Supplements(1)

Supplementary Information-10.1007s12613-023-2691-9.doc

References(40)

References

[1]	C. Yang, S. Xin, L.Q. Mai, and Y. You, Materials design for high-safety sodium-ion battery, Adv. Energy Mater., 11(2021), No. 2, art. No. 2000974. doi: 10.1002/aenm.202000974
[2]	K.M. Abraham, How comparable are sodium-ion batteries to lithium-ion counterparts? ACS Energy Lett., 5(2020), No. 11, p. 3544. doi: 10.1021/acsenergylett.0c02181
[3]	C.L. Zhao, Q.D. Wang, Z.P. Yao, et al., Rational design of layered oxide materials for sodium-ion batteries, Science, 370(2020), No. 6517, p. 708. doi: 10.1126/science.aay9972
[4]	L. Xue, X.Q. Shi, B.W. Lin, Q.B. Guo, Y. Zhao, and H. Xia, Self-standing P2/P3 heterostructured Na_0.7CoO₂ nanosheet arrays as 3D cathodes for flexible sodium-ion batteries, J. Power Sources, 457(2020), art. No. 228059. doi: 10.1016/j.jpowsour.2020.228059
[5]	X. Zhou, A.L. Zhao, Z.X. Chen, and Y.L. Cao, Research progress of tunnel-structural Na_0.44MnO₂ cathode for sodium-ion batteries: A mini review, Electrochem. Commun., 122(2021), art. No. 106897. doi: 10.1016/j.elecom.2020.106897
[6]	J. Peng, W. Zhang, Q.N. Liu, et al., Prussian blue analogues for sodium-ion batteries: Past, present, and future, Adv. Mater., 34(2022), No. 15, art. No. e2108384. doi: 10.1002/adma.202108384
[7]	L. Xu, H. Li, T. Du, et al., An all Prussian blue analog-based aprotic sodium-ion battery, Battery Energy, 1(2022), No. 2, art. No. 20210003. doi: 10.1002/bte2.20210003
[8]	H. Zhang, J. Peng, L. Li, et al., Low-cost zinc substitution of iron-based Prussian blue analogs as long lifespan cathode materials for fast charging sodium-ion batteries, Adv. Funct. Mater., 33(2023), No. 2, art. No. 2210725. doi: 10.1002/adfm.202210725
[9]	L. Chen, Z.Q. Zhong, S.B. Ren, and D.M. Han, Carbon-coated Na₃V₂(PO₄)₃ supported on multiwalled carbon nanotubes for half-/ full-cell sodium-ion batteries, Energy Technol., 8(2020), No. 3, art. No. 1901080. doi: 10.1002/ente.201901080
[10]	V. Priyanka, G. Savithiri, R. Subadevi, and M. Sivakumar, An emerging electrochemically active maricite NaMnPO₄ as cathode material at elevated temperature for sodium-ion batteries, Appl. Nanosci., 10(2020), No. 10, p. 3945. doi: 10.1007/s13204-020-01506-8
[11]	W. Chang, X.Y. Zhang, J. Qu, et al., Freestanding Na₃V₂O₂(PO₄)₂F/graphene aerogels as high-performance cathodes of sodium-ion full batteries, ACS Appl. Mater. Interfaces, 12(2020), No. 37, p. 41419. doi: 10.1021/acsami.0c11074
[12]	D. Ledwoch, J.B. Robinson, D. Gastol, et al., Hard carbon composite electrodes for sodium-ion batteries with nano-zeolite and carbon black additives, Batteries Supercaps, 4(2021), No. 1, p. 163. doi: 10.1002/batt.202000161
[13]	W. Sun, Q. Sun, R.F. Lu, et al., Sodium hypophosphite-assist pyrolysis of coal pitch to synthesis P-doped carbon nanosheet anode for ultrafast and long-term cycling sodium-ion batteries, J. Alloys Compd., 889(2021), art. No. 161678. doi: 10.1016/j.jallcom.2021.161678
[14]	Y.H. Liu, Q.Z. Liu, C. Jian, et al., Red-phosphorus-impregnated carbon nanofibers for sodium-ion batteries and liquefaction of red phosphorus, Nat. Commun., 11(2020), art. No. 2520. doi: 10.1038/s41467-020-16077-z
[15]	X. Wu, X.X. Lan, R.Z. Hu, Y. Yao, Y. Yu, and M. Zhu, Tin-based anode materials for stable sodium storage: Progress and perspective, Adv. Mater., 34(2022), No. 7, art. No. 2106895. doi: 10.1002/adma.202106895
[16]	H. Chen, B.B. Xu, Q.S. Ping, et al., Co₂B₂O₅ as an anode material with high capacity for sodium ion batteries, Rare Met., 39(2020), No. 9, p. 1045. doi: 10.1007/s12598-020-01383-8
[17]	H. Qiu, H.Y. Zheng, Y.H. Jin, et al., Mesoporous cubic SnO₂–CoO nanoparticles deposited on graphene as anode materials for sodium ion batteries, J. Alloys Compd., 874(2021), art. No. 159967. doi: 10.1016/j.jallcom.2021.159967
[18]	L. Coustan, J.M. Tarascon, and C. Laberty-Robert, Thin fiber-based separators for high-rate sodium ion batteries, ACS Appl. Energy Mater., 2(2019), No. 12, p. 8369. doi: 10.1021/acsaem.9b01821
[19]	S. Janakiraman, A. Surendran, S. Ghosh, S. Anandhan, and A. Venimadhav, Electroactive poly(vinylidene fluoride) fluoride separator for sodium ion battery with high coulombic efficiency, Solid State Ionics, 292(2016), p. 130. doi: 10.1016/j.ssi.2016.05.020
[20]	M.H. Li, G.J. Lu, W.K. Zheng, et al., Multifunctionalized safe separator toward practical sodium-metal batteries with high-performance under high mass loading, Adv. Funct. Mater., 33(2023), No. 26, art. No. 2214759. doi: 10.1002/adfm.202214759
[21]	Y. Ansari, B.K. Guo, J.H. Cho, et al., Low-cost, dendrite-blocking polymer–Sb₂O₃ separators for lithium and sodium batteries, J. Electrochem. Soc., 161(2014), No. 10, p. A1655. doi: 10.1149/2.0631410jes
[22]	L.P. Zhang, X.L. Li, M.R. Yang, and W.H. Chen, High-safety separators for lithium-ion batteries and sodium-ion batteries: Advances and perspective, Energy Storage Mater., 41(2021), p. 522. doi: 10.1016/j.ensm.2021.06.033
[23]	T.M. Zhu, X.X. Zuo, X.X. Lin, et al., High-wettability composite separator embedded with in situ grown TiO₂ nanoparticles for advanced sodium-ion batteries, Energy Technol., 10(2022), No. 10, art. No. 2200409. doi: 10.1002/ente.202200409
[24]	D. Zhou, X.A. Tang, X. Guo, et al., Polyolefin-based Janus separator for rechargeable sodium batteries, Angew. Chem. Int. Ed., 59(2020), No. 38, p. 16725. doi: 10.1002/anie.202007008
[25]	X.H. Ma, F. Qiao, M.F. Qian, et al., Facile fabrication of flexible electrodes with poly(vinylidene fluoride)/Si₃N₄ composite separator prepared by electrospinning for sodium-ion batteries, Scripta Mater., 190(2021), p. 153. doi: 10.1016/j.scriptamat.2020.08.053
[26]	H.C. Gao, B.K. Guo, J. Song, K. Park, and J.B. Goodenough, A composite gel–polymer/glass–fiber electrolyte for sodium-ion batteries, Adv. Energy Mater, 5(2015), No. 9, art. No. 1402235. doi: 10.1002/aenm.201402235
[27]	J.I. Kim, Y. Choi, K.Y. Chung, and J.H. Park, A structurable gel–polymer electrolyte for sodium ion batteries, Adv. Funct. Mater., 27(2017), No. 34, art. No. 1701768. doi: 10.1002/adfm.201701768
[28]	P.C. Ani, P.U. Nzereogu, A.C. Agbogu, F.I. Ezema, and A.C. Nwanya, Cellulose from waste materials for electrochemical energy storage applications: A review, Appl. Surf. Sci. Adv., 11(2022), art. No. 100298. doi: 10.1016/j.apsadv.2022.100298
[29]	J.L. Yang, X.X. Zhao, W. Zhang, et al., Inside back cover: “pore-hopping” ion transport in cellulose-based separator towards high-performance sodium-ion batteries, Angew. Chem. Int. Ed., 62(2023), No. 15, art. No. 202302568. doi: 10.1002/anie.202302568
[30]	H.Y. Zhou, J. Gu, W.W. Zhang, C.S. Hu, and X.Y. Lin, Rational design of cellulose nanofibrils separator for sodium-ion batteries, Molecules, 26(2021), No. 18, art. No. 5539. doi: 10.3390/molecules26185539
[31]	T.W. Zhang, B. Shen, H.B. Yao, et al., Prawn shell derived chitin nanofiber membranes as advanced sustainable separators for Li/Na-ion batteries, Nano Lett., 17(2017), No. 8, p. 4894. doi: 10.1021/acs.nanolett.7b01875
[32]	C.Y. Cao, H.B. Wang, W.W. Liu, X.Z. Liao, and L. Li, Nafion membranes as electrolyte and separator for sodium-ion battery, Int. J. Hydrogen Energy, 39(2014), No. 28, p. 16110. doi: 10.1016/j.ijhydene.2013.12.119
[33]	V.C. Ho, B.T.D. Nguyen, H.Y.N. Thi, J.F. Kim, and J. Mun, Poly(dopamine) surface-modified polyethylene separator with electrolyte-philic characteristics for enhancing the performance of sodium-ion batteries, Int. J. Energy Res., 46(2022), No. 4, p. 5177. doi: doi.org/10.1002/er.7510
[34]	Y.S. Zhu, F.X. Wang, L.L. Liu, S.Y. Xiao, Y.Q. Yang, and Y.P. Wu, Cheap glass fiber mats as a matrix of gel polymer electrolytes for lithium ion batteries, Sci. Rep., 3(2013), art. No. 3187. doi: 10.1038/srep03187
[35]	J.Y. Zheng, X.L. Liu, Y.L. Duan, et al., Stable cross-linked gel terpolymer electrolyte containing methyl phosphonate for sodium ion batteries, J. Membr. Sci., 583(2019), p. 163. doi: 10.1016/j.memsci.2019.04.044
[36]	X.H. Ma, Z.H. Zheng, T.W. Zhang, et al., Rational design of glass fiber-cellulose composite separator for sodium-ion batteries, Scripta Mater., 232(2023), art. No. 115481. doi: 10.1016/j.scriptamat.2023.115481
[37]	R. Arunkumar, A.P. Vijaya Kumar Saroja, and R. Sundara, Barium titanate-based porous ceramic flexible membrane as a separator for room-temperature sodium-ion battery, ACS Appl. Mater. Interfaces, 11(2019), No. 4, p. 3889. doi: 10.1021/acsami.8b17887
[38]	S. Janakiraman, A. Agrawal, R. Biswal, and A. Venimadhav, An amorphous polyvinylidene fluoride-co-hexafluoropropylene based gel polymer electrolyte for sodium-ion cells, Appl. Surf. Sci. Adv., 6(2021), art. No. 100139. doi: 10.1016/j.apsadv.2021.100139
[39]	D.N. Lei, Y.B. He, H.J. Huang, et al., Cross-linked beta alumina nanowires with compact gel polymer electrolyte coating for ultra-stable sodium metal battery, Nat. Commun., 10(2019), No. 1, art. No. 4244. doi: 10.1038/s41467-019-11960-w
[40]	N. Mittal, S.A. Tien, E. Lizundia, and M. Niederberger, Hierarchical nanocellulose-based gel polymer electrolytes for stable Na electrodeposition in sodium ion batteries, Small, 18(2022), No. 43, art. No. 2107183. doi: 10.1002/smll.202107183