留言板

尊敬的读者、作者、审稿人, 关于本刊的投稿、审稿、编辑和出版的任何问题, 您可以本页添加留言。我们将尽快给您答复。谢谢您的支持!

姓名
邮箱
手机号码
标题
留言内容
验证码
Volume 15 Issue 4
Aug.  2008
数据统计

分享

计量
  • 文章访问数:  237
  • HTML全文浏览量:  49
  • PDF下载量:  8
  • 被引次数: 0
Haiqing Yin, Xuanhui Qu,  and Chengchang Jia, Fabrication of micro gear wheels by micropowder injection molding, J. Univ. Sci. Technol. Beijing, 15(2008), No. 4, pp. 480-483. https://doi.org/10.1016/S1005-8850(08)60090-0
Cite this article as:
Haiqing Yin, Xuanhui Qu,  and Chengchang Jia, Fabrication of micro gear wheels by micropowder injection molding, J. Univ. Sci. Technol. Beijing, 15(2008), No. 4, pp. 480-483. https://doi.org/10.1016/S1005-8850(08)60090-0
引用本文 PDF XML SpringerLink
Materials

Fabrication of micro gear wheels by micropowder injection molding

  • 通讯作者:

    Haiqing Yin    E-mail: hqyin@mater.ustb.edu.cn

  • The micropowder injection molding technology was investigated to fabricate the microsized gear wheels on a conventional injection molding machine. The feedstock comprised of carbonyl ferrum powder and a wax-based thermoplastic binder. Microinjection molding was fulfilled at about 423 K under 100 MPa. The heating system was applied to the die to improve the fluidity of the feedstock and subsequently the cooling system was used to enhance the strength of the green compacts after injection by decreasing the temperature of the die. The gear wheels were realized successfully with their addendum circle diameter ranging from 800 to 200 um and with the center hole as small as 60 um.
  • Materials

    Fabrication of micro gear wheels by micropowder injection molding

    + Author Affiliations
    • The micropowder injection molding technology was investigated to fabricate the microsized gear wheels on a conventional injection molding machine. The feedstock comprised of carbonyl ferrum powder and a wax-based thermoplastic binder. Microinjection molding was fulfilled at about 423 K under 100 MPa. The heating system was applied to the die to improve the fluidity of the feedstock and subsequently the cooling system was used to enhance the strength of the green compacts after injection by decreasing the temperature of the die. The gear wheels were realized successfully with their addendum circle diameter ranging from 800 to 200 um and with the center hole as small as 60 um.
    • loading

    Catalog


    • /

      返回文章
      返回