Jun Wang, Nan Li, Caicheng Shi, and Chengchang Jia, β-Sialon Produced by Carbon Thermal Nitriding Reaction of Bauxite, J. Univ. Sci. Technol. Beijing, 7(2000), No. 3, pp. 209-213.
Cite this article as:
Jun Wang, Nan Li, Caicheng Shi, and Chengchang Jia, β-Sialon Produced by Carbon Thermal Nitriding Reaction of Bauxite, J. Univ. Sci. Technol. Beijing, 7(2000), No. 3, pp. 209-213.
Jun Wang, Nan Li, Caicheng Shi, and Chengchang Jia, β-Sialon Produced by Carbon Thermal Nitriding Reaction of Bauxite, J. Univ. Sci. Technol. Beijing, 7(2000), No. 3, pp. 209-213.
Citation:
Jun Wang, Nan Li, Caicheng Shi, and Chengchang Jia, β-Sialon Produced by Carbon Thermal Nitriding Reaction of Bauxite, J. Univ. Sci. Technol. Beijing, 7(2000), No. 3, pp. 209-213.
Material Science and Engineering School, University of Science and Technology Beijing, Beijing 100083, China
Material Science and Engineering School, Wuhan University of Science and Technology, Wuhan 430081, China
中文摘要
β-Sialon was produced by carbon thermal nitriding reaction in N2 gas atmosphere when the mixtures of bauxite and anthracite were put into vertical furnace. According to the mass loss of raw materials and the result of X-ray diffration (XRD) of products, the influences of the process parameters on the compositions and relative contents of products, such as the fixed carbon content, the flow of N2, the soaking time and the temperature, were researched.
β-Sialon was produced by carbon thermal nitriding reaction in N2 gas atmosphere when the mixtures of bauxite and anthracite were put into vertical furnace. According to the mass loss of raw materials and the result of X-ray diffration (XRD) of products, the influences of the process parameters on the compositions and relative contents of products, such as the fixed carbon content, the flow of N2, the soaking time and the temperature, were researched.