Peng Zhang, Yunhui Du, Hanwu Liu, Shuming Xing, Daben Zeng, Jianzhong Cui, and Limin Ba, Thickness of compound layer in steel-aluminum solid to liquid bonding, J. Univ. Sci. Technol. Beijing, 10(2003), No. 5, pp. 48-52.
Cite this article as:
Peng Zhang, Yunhui Du, Hanwu Liu, Shuming Xing, Daben Zeng, Jianzhong Cui, and Limin Ba, Thickness of compound layer in steel-aluminum solid to liquid bonding, J. Univ. Sci. Technol. Beijing, 10(2003), No. 5, pp. 48-52.
引用本文 PDF XML SpringerLink
Materials

Thickness of compound layer in steel-aluminum solid to liquid bonding

  • 通讯作者:

    Peng Zhang    E-mail: Zhangp9@263.net

  • The bonding of solid steel plate to liquid aluminum was studied using rapid solidification. The surface of solid steel plate was defatted, descaled, immersed (in K2ZrF6 flux aqueous solution) and stoved. In order to determine the thickness of Fe-Al compound layer at the interface of steel-aluminum solid to liquid bonding under rapid solidification, the interface of bonding plate was investigated by SEM (Scanning Electron Microscope) experiment. The relationship between bonding parameters (such as preheat temperature of steel plate, temperature of aluminum liquid and bonding time) and thickness of Fe-Al compound layer at the interface was established by artificial neural networks (ANN) perfectly. The maximum of relative error between the output and the desired output of the ANN is only 5.4%. From the bonding parameters for the largest interfacial shear strength of bonding plate (226℃ for preheat temperature of steel plate, 723℃ for temperature of aluminum liquid and 15.8 s for bonding time), the reasonable thickness of Fe-Al compound layer 10.8 μm was got.
  • Materials

    Thickness of compound layer in steel-aluminum solid to liquid bonding

    + Author Affiliations
    • The bonding of solid steel plate to liquid aluminum was studied using rapid solidification. The surface of solid steel plate was defatted, descaled, immersed (in K2ZrF6 flux aqueous solution) and stoved. In order to determine the thickness of Fe-Al compound layer at the interface of steel-aluminum solid to liquid bonding under rapid solidification, the interface of bonding plate was investigated by SEM (Scanning Electron Microscope) experiment. The relationship between bonding parameters (such as preheat temperature of steel plate, temperature of aluminum liquid and bonding time) and thickness of Fe-Al compound layer at the interface was established by artificial neural networks (ANN) perfectly. The maximum of relative error between the output and the desired output of the ANN is only 5.4%. From the bonding parameters for the largest interfacial shear strength of bonding plate (226℃ for preheat temperature of steel plate, 723℃ for temperature of aluminum liquid and 15.8 s for bonding time), the reasonable thickness of Fe-Al compound layer 10.8 μm was got.