Hai-yan Tangand Jing-she Li, Thermodynamic analysis on the formation mechanism of MgO·Al2O3 spinel type inclusions in casing steel, Int. J. Miner. Metall. Mater., 17(2010), No. 1, pp. 32-38. https://doi.org/10.1007/s12613-010-0106-1
Cite this article as:
Hai-yan Tangand Jing-she Li, Thermodynamic analysis on the formation mechanism of MgO·Al2O3 spinel type inclusions in casing steel, Int. J. Miner. Metall. Mater., 17(2010), No. 1, pp. 32-38. https://doi.org/10.1007/s12613-010-0106-1

Thermodynamic analysis on the formation mechanism of MgO·Al2O3 spinel type inclusions in casing steel

+ Author Affiliations
  • Corresponding author:

    Hai-yan Tang    E-mail: tanghaiyan@metall.ustb.edu.cn

  • Received: 21 December 2008Revised: 19 January 2009Accepted: 7 February 2009
  • MgO·Al2O3 spinel type inclusions in casing steel were analyzed by scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). The results show that there are three forms. One is pure MgO·Al2O3 spinel, another is the composite oxide of the Mg-Al-Ca-Si-O system, and the third is the complex with oxide as a core covered by sulfide. The formation mechanisms were studied. The influences of slag basicity and vacuum degree on the magnesium content during the vacuum treatment of molten steel and furnace lining in molten steel were calculated with the coexistence theory of slag structure. The results show that the magnesium content increases with the increase in slag basicity and aluminum content in molten steel, and decreases with the increase in CO partial pressure.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(239) PDF Downloads(9) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return