Bin Liu and Fu Guo, Electrical conductivity changes of bulk tin and Sn-3.0Ag-0.5Cu in bulk and in joints during isothermal aging, Int. J. Miner. Metall. Mater., 17(2010), No. 4, pp. 453-458. https://doi.org/10.1007/s12613-010-0340-6
Cite this article as:
Bin Liu and Fu Guo, Electrical conductivity changes of bulk tin and Sn-3.0Ag-0.5Cu in bulk and in joints during isothermal aging, Int. J. Miner. Metall. Mater., 17(2010), No. 4, pp. 453-458. https://doi.org/10.1007/s12613-010-0340-6

Electrical conductivity changes of bulk tin and Sn-3.0Ag-0.5Cu in bulk and in joints during isothermal aging

+ Author Affiliations
  • Corresponding author:

    Bin Liu    E-mail: lbin130@emails.bjut.edu.cn

  • Received: 21 July 2009Revised: 2 August 2009Accepted: 15 August 2009
  • The changes of electrical conductivity (resistance) between Sn-3.0Ag-0.5Cu solder joints and printed circuit board (PCB) assembly during aging at 125℃ were investigated by the four-point probe technique. The microstructural characterizations of interfacial layers between the solder matrix and the substrate were examined by optical microscopy and scanning electronic microscopy. Different types of specimens were designed to consider several factors. The experimental results indicate that electrical conductivities (resistances) and residual shear strengths of the solder joint specimens significantly decrease after 1000 h during isothermal aging. Microcracks generate in the solder matrix at the first 250 h. Besides, the evolutions of microstructural characterizations at the interface and the matrix of solder joints were noted in this research.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(261) PDF Downloads(13) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return