Kinetics of recrystallization for twin-roll casting AZ31 magnesium alloy during homogenization

The kinetics of recrystallization for twin-roll casting AZ31 magnesium alloy with different thicknesses during homogenization was analyzed. It is shown that fine grains are first formed at the boundaries of deformed bands in the twin-roll casting slab. The recrystallized grains with no strain are gradually substituted for the deformed microstructure of twin-roll casting AZ31 magnesium alloy. The incubation temperature and time for the recrystallization of a twin-roll casting AZ31 magnesium alloy strip with a thickness of 3 mm are lower and shorter than those of the 6-mm thick strip, respectively. The 3-mm thick twin-roll casting magnesium alloy has finer grains than the 6-mm thick strip. The activation energies of recrystallization for twin-roll casting AZ31 magnesium alloy slabs with the thickness of 3 and 6 mm are 88 and 69 kJ/mol, respectively. The kinetics curves of recrystallization for twin-roll casting AZ31 magnesium alloy were obtained.