Tai-he Wang, Wei-jia Song, Rong Li,  and Qiang Zhen, Fluorite Ce0.8Sm0.2O2-δ porous layer coating to enhance the oxygen permeation behavior of a BaCo0.7Fe0.2Nb0.1O3-δ mixed conductor, Int. J. Miner. Metall. Mater., 23(2016), No. 6, pp. 698-703. https://doi.org/10.1007/s12613-016-1283-3
Cite this article as:
Tai-he Wang, Wei-jia Song, Rong Li,  and Qiang Zhen, Fluorite Ce0.8Sm0.2O2-δ porous layer coating to enhance the oxygen permeation behavior of a BaCo0.7Fe0.2Nb0.1O3-δ mixed conductor, Int. J. Miner. Metall. Mater., 23(2016), No. 6, pp. 698-703. https://doi.org/10.1007/s12613-016-1283-3

Fluorite Ce0.8Sm0.2O2-δ porous layer coating to enhance the oxygen permeation behavior of a BaCo0.7Fe0.2Nb0.1O3-δ mixed conductor

+ Author Affiliations
  • Corresponding authors:

    Rong Li    E-mail: li-rong@shu.edu.cn

    Qiang Zhen    E-mail: qzhen@staff.shu.edu.cn

  • Received: 16 November 2015Revised: 4 January 2016Accepted: 12 January 2016
  • Fluorite Ce0.8Sm0.2O2-δ (SDC) nanopowder with a crystallite size of 15 nm was synthesized by a co-precipitation method. An SDC porous layer was coated onto a BaCo0.7Fe0.2Nb0.1O3-δ (BCFN) mixed conductor to improve its oxygen transport behavior. The results show that the SDC-coated BCFN membrane exhibits a remarkably higher oxygen permeation flux (JO2) than the uncoated BCFN in the partial oxidation of coke oven gas (COG). The maximum (JO2) value of the SDC-coated BCFN is 18.28 mL·min-1·cm-2 under a COG/air flux of 177 mL·min-1/353 mL·min-1 at 875℃ when the thickness of the BCFN membrane is 1 mm; this (JO2) value is 23% higher than that of the uncoated BCFN membrane. This enhancement is likely because of the higher oxygen ionic conductivity of SDC, which supplies oxygen vacancies and accelerates oxygen exchange on the membrane/coating layer/gas three-phase boundary.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(250) PDF Downloads(7) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return