Peculiarity of magnetoresistance of discontinuous ferromagnetic thin films

Yu. O. Shkurdoda; I. M. Pazukha; A. M. Chornous

doi:10.1007/s12613-017-1539-6

Volume 24 Issue 12

Dec. 2017

Turn off MathJax

Article Contents

Article Navigation > International Journal of Minerals, Metallurgy and Materials > 2017 > 24(12): 1459-1463

Yu. O. Shkurdoda, I. M. Pazukha, and A. M. Chornous, Peculiarity of magnetoresistance of discontinuous ferromagnetic thin films, Int. J. Miner. Metall. Mater., 24(2017), No. 12, pp. 1459-1463. https://doi.org/10.1007/s12613-017-1539-6

Cite this article as:

Yu. O. Shkurdoda, I. M. Pazukha, and A. M. Chornous, Peculiarity of magnetoresistance of discontinuous ferromagnetic thin films, Int. J. Miner. Metall. Mater., 24(2017), No. 12, pp. 1459-1463. https://doi.org/10.1007/s12613-017-1539-6

Citation:

PDF( 1424 KB)

Research Article

Peculiarity of magnetoresistance of discontinuous ferromagnetic thin films

+ Author Affiliations

Received: 27 February 2017; Revised: 11 May 2017; Accepted: 12 May 2017

Abstract

Abstract

The magnetoresistive properties of discontinuous ferromagnetic Fe and Co thin films deposited by electron-beam sputtering onto glass substrates at room temperature were investigated. Tunnel magnetoresistance (MR) was observed for all of the as-deposited samples. The maximum MR was observed for Fe thin films with an effective thickness of 17 nm. In the case of the Co thin films, the annealing process led to a change of the type of MR to anisotropic at Co film thicknesses (d_Co) of 15 ≤ d_Co ≤ 25 nm and to positive isotropic at thicknesses of d_Co < 15 nm. By contrast, the MR type of Fe thin films did not change.
- discontinuous thin films;
- ferromagnetic;
- structure;
- magnetoresistance;
- peculiarity

FullText(HTML)

Supplements(0)

References(20)

References

[1]	M.N. Baibich, J.M. Broto, A. Fert, N.F. Van Dau, F. Petroff, P. Eitenne, G. Creuzet, A. Freiderich, and J. Chazelas, Giant magnetoresistance of (001)Fe/(001)Cr magnetic super-lattices, Phys. Rev. Lett., 61(1988), No. 21, p. 2472.
[2]	G. Chen, C. Song, and F. Pan, Magnetoresistive sensors with hybrid Co/insulator/ZnO:Co junctions, Int. J. Miner. Metall. Mater., 20(2013), No. 2, p. 160.
[3]	S.a. Nepijko, D. Kutnyakhov, S.I. Protsenko, L.V. Odnodvorets, and G. Schonhense, Sensor and microelectronic elements based on nanoscale granular systems, J. Nanopart. Res., 13(2011), No. 12, p. 6263.
[4]	C. Franz, M. Czerner, and C. Heliger, Influence of the magnetic material on tunneling magnetoresistance and spin transfer torque in tunnel junctions:Ab initio studies, Phys. Rev. B, 88(2013), p.1081.
[5]	A.Y. Vovk, J.Q. Wang, A.M. Pogoriliy, O.V. Shypil, and A.F. Kravets, Magneto-transport properties of CoFe-Al₂O₃ granular films in the vicinity of the percolation threshold, J. Magn. Magn. Mater., 242-245(2002), p. 476.
[6]	G. Herzog, S. Krause, and R. Wiesendanger, Heat assisted spin torque switching of quasi stable nanomagnets across a vacuum gap, Appl. Phys. Lett., 96(2010), No. 10, art. No. 102505.
[7]	A. M. Chornous, Y.O. Shkurdoda, V.B. Loboda, Y.M. Shabelnyk, and V.O. Kravchenko, Influence of the surface morphology on the magnetoresistance of ultrathin films of ferromagnetic metals and their alloys, Eur. Phys. J. Plus, 132(2017), No. 1, p. 58.
[8]	V.B. Loboda, V.M. Kolomiets, Y.O. Shkurdoda, V.O. Kravchenko, and L.V. Dekhtyaruk, Structure and magnetoresistive properties of nanocrystalline film systems based on Co, Fe, Ag, and Cu, Metallofiz. Noveishie Tekhnol., 34(2012), No. 8, p. 1043.
[9]	V. Ilkovič, Comparison of the effect of the exchange and single-ion anisotropy on the magnetic properties of thin ferromagnetic films, J. Magn. Magn. Mater., 402(2016), p. 196.
[10]	S.Y. Wang, T.J. Gao, C.T. Wang, and J.F. He, Studies of anisotropic magnetoresistance and magnetic property of Ni₈₁Fe₁₉ ultra-thin films with the lower base vacuum, J. Alloys Compd., 554(2013), p. 405.
[11]	I.M. Lytvynenko, I.M. Pazukha, and V.V. Bibyk, Structural, magnetic and magnetoresistive properties of ternary film Ni-Fe-Co alloy, J. Nano-Electron. Phys., 6(2014), No. 2, art. No. 2014.
[12]	J.Z. Sun and D.C. Ralph, Magnetoresistance and spin-transfer torque in magnetic tunnel junctions, J. Magn. Magn. Mater., 320(2008), No. 7, p. 1227.
[13]	G.N. Kakazei, Y.G. Pogorelov, A.M.L. Lopes, J.B. Sousa, S.Cardoso, P.P.Freitas, M.M. Pereira de Azevedo, and E. Snoeck, Tunnel magnetoresistance and magnetic ordering in ion-beam sputtered Co₈₀Fe₂₀/Al₂O₃ discontinuous multilayers, J. Appl. Phys., 90(2001), No. 8, p. 4044.
[14]	I.M. Lytvynenko, I.M. Pazukha, O.V. Pylypenko, and V.V. Bibyk, Structural-phase state, magnetoresistive and magnetic properties of permalloy films, Metallofiz. Noveishie Tekhnol., 37(2015), No. 10, p. 1377.
[15]	O.V. Snigirev, A.M. Tishin, K.E. Andreev, S.A. Gudoshnikov, and J. Bohr, Magnetic properties of ultrathin Ni films, Phys. Solid State, 40(1998), No. 9, p. 1530.
[16]	R. Koch, D. Hu, and A.K. Das, Compressive stress in polycrystalline volmer-weber films, Phys. Rev. Lett., 94(2005), No. 14, art. No. 146101.
[17]	A.E. Varfolomeev and M.V. Sedova, Large positive magnetoresistance effect in metal-insulator nanocomposites in weak magnetic fields, Phys. Solid State, 45(2003), No. 3, p. 529.
[18]	O.V. Stogneĭ, A.V. Sitnikov, Y.E. Kalinin, S.F. Avdeev, and M.N. Kopytin, Isotropic positive magnetoresistance in Co-Al₂O_n nanocomposites, Phys. Solid State, 49(2007), No. 1, p. 164.
[19]	A.A. Timofeev, S.M. Ryabchenko, A.F. Lozenko, P.A. Trotsenko, O.V. Stogneĭ, A.V. Sitnikov, and S.F. Avdeev, Investigations of the magnetic properties of the granular system Co_0.6(Al₂O_n)_0.4 possessing isotropic positive magnetoresistance, Low Temp. Phys., 33(2007), No. 11, p. 974.
[20]	A.S. Andreenko, V.A. Berezovets, A.B. Granovskii, I.V. Zolotukhin, M. Inoue, Y.E. Kalinin, A.V. Sitnikov, O.V. Stognei, and T. Palevski, Inverse magnetoresistance in (FeCoB)-(Al₂O₃) magnetic granular composites, Phys. Solid State, 45(2003), No. 8, p. 1519.