Characteristics of microstructural evolution during deformation-enhanced ferrite transformation in Nb-microalloyed HSLA steel

+ Author Affiliations
  • Microstructure evolution during deformation of undercooled austenite at 760℃ was investigated in Nb-microalloyed steel by using SEM (scanning electron microscope), TEM (transmission electron microscope), and EBSD (electron backscattered diffraction). It is indicated that during deformation-enhanced ferrite transformation (DEFT) in Nb-microalloyed steel, the incubation period is prolonged, and the higher strain is needed to accomplish ferrite transformation. Therefore, the transformation kinetics curves move to high strain parallelly; and the transformation kinetics curves of Nb-microalloyed steel can be divided into three stages. At the fast stage, the solute drag effect of Nb and the consumption of strain energy for the dynamic precipitation of Nb(CN) led to a long incubation period, and at the second stage, ferrite transformation was accelerated significantly and fine Nb(CN) precipitates restrict the grain growth of ferrite effectively. The results also showed that DEFT in Nb-microalloyed steel is still a nucleation dominated process, and during the microstructure evolution the interchange of 〈001〉 and 〈111〉 texture was obtained.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(184) PDF Downloads(11) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return