Gelcasting of 316L stainless steel

+ Author Affiliations
  • Corresponding author:

    Yan Li    E-mail: yanli79@sohu.com

  • Received: 15 December 2006
  • A novel near-net process, gelcasting, was successfully used to prepare larger size 316L stainless steel parts with complex shape. In this study, the effects of process parameters on the viscosity of the slurry and the dry green strength were investigated. The results show that gas atomization (GA) powder is more suitable for gelcasting compared with water atomization (WA) powder. The maximum solid loading is 55vo1% for ball-milled slurry with GA powders. And the optimum amounts of monomers (acrylamide (AM)+methylenebisacrylamide (MBAM); the mass ratio, 30:1) and initiator in the AM system are 1.8% (based on the weight of metal powder) and 0.8%-1.4% (based on the weight of monomers), respectively, at which, the maximum green strength obtained is 33.7 MPa. The mechanical properties of the sintered specimen are as follows: ultimate tensile strength, 493 MPa; yield strength, 162 MPa; and HRB, 72.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(234) PDF Downloads(13) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return