Purity of SiC powders fabricated by coat-mix

+ Author Affiliations
  • Silicon carbide powders were synthesized by the coat-mix process, with phenolic resin and silicon powders as starting materials. The effects of synthetic conditions, including sintering temperature and the molar ratio of resin-derived carbon to silicon on the composition and the purity of the resultant powders were investigated. The results show that a higher sintering temperature and an appropriate molar ratio of resin-derived carbon to silicon are favorable for producing high purity silicon carbide powders. It is found that the silicon carbide content increases slightly with increasing the sintering temperature during the solid-solid reaction. The temperature gradient plays an important role on this trend. When the sintering temperature is raised up to 1500℃, the formation of silicon earbide is based on the liquid-solid reaction, and high purity (99.8wt%) silicon carbide powders can easily be obtained. It can also be found that the optimum molar ratio of resin-derived carbon to silicon is 1:1.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(356) PDF Downloads(7) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return