Hai Lin, Ying-bo Dong,  and Le-yong Jiang, Preparation of calcium carbonate particles coated with titanium dioxide, Int. J. Miner. Metall. Mater., 16(2009), No. 5, pp. 592-597. https://doi.org/10.1016/S1674-4799(09)60102-3
Cite this article as:
Hai Lin, Ying-bo Dong,  and Le-yong Jiang, Preparation of calcium carbonate particles coated with titanium dioxide, Int. J. Miner. Metall. Mater., 16(2009), No. 5, pp. 592-597. https://doi.org/10.1016/S1674-4799(09)60102-3
Materials

Preparation of calcium carbonate particles coated with titanium dioxide

+ Author Affiliations
  • The preparation of a new mineral composite material, calcium carbonate particles coated with titanium dioxide, was studied. The mechanism of the preparation process was proposed. The new mineral composite material was made by the mechanoehemieal method under the optimum condition that the mass ratio of calcium carbonate particles to titanium dioxide was 6.5:3.5. The mass ratios of two different types of titanium dioxide (anatase to rutile) and grinding media to grinded materials were 8:2 and 4:1 respectively, and the modified density was 60%. Under this condition, the new material was capable of forming after 120-min modification. The hiding power and oil absorption of this new material were 29.12 g/m2 and 23.30%, respectively. The results show that the modification is based on surface hydroxylation. After coating with titanium dioxide, the hiding power of calcium carbonate can be improved greatly. The new mineral composite materials can be used as the substitute for titanium dioxide.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(435) PDF Downloads(19) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return