WANG Xinhua, WANG Wenjun, WU Dongmei, CHANG Bo, LIU Xinyu, ZHANG Li,  and YE Jinwei, Preventing Occurrence of Transverse Corner Cracks on Nb, V and Ti Microalloying Steel CC Slabs, J. Univ. Sci. Technol. Beijing, 4(1997), No. 4, pp. 5-9.
Cite this article as:
WANG Xinhua, WANG Wenjun, WU Dongmei, CHANG Bo, LIU Xinyu, ZHANG Li,  and YE Jinwei, Preventing Occurrence of Transverse Corner Cracks on Nb, V and Ti Microalloying Steel CC Slabs, J. Univ. Sci. Technol. Beijing, 4(1997), No. 4, pp. 5-9.

Preventing Occurrence of Transverse Corner Cracks on Nb, V and Ti Microalloying Steel CC Slabs

+ Author Affiliations
  • Received: 21 June 1997
  • Based on their hot ductilities, Nb, V and Ti microalloying steels can be classified into two groups. The first group includes steels with lower carbon content (≤0.10%). Ductilities of steels of this group recover and rise with decreasing temperature when temperature lowers to below 825℃. Another group includes steels which contain more carbon (>0.12%) or contain more Nb and V. The low ductility temperature Region Ⅲ for steels of mis group extends to temperature as low as 725℃. The occurrence of the transverse corner cracks of the Nb, V and Ti microalloying steel CC slabs has be considerably decreased by stabilizing casting speed, increasing mold steel level automatic control ratio,enhancing caster segment radial alignment and adopting proper secondary cooling patterns to make slab corner temperature at straightening out off the low ductility temperature region.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(316) PDF Downloads(11) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return