Formation mechanism of internal cracks in continuously cast slab

In order to make clear the formation mechanism of centerline cracks in continuously cast slabs, the form, distribution and other characteristics of the cracks were analyzed. The final solidification point, surface temperature of the slabs and strain in solidifying shell were investigated. The results were that: (1) Five relatively low temperature zones exist on slab surface below the three water spraying nozzles and near the two edges, respectively, which corresponds to the places of centerline cracks and triangle-zone cracks. (2) Centerline cracks and triangle-zone cracks occur because of weak secondary cooling, uneven cooling along slab width,and large variation of roll gap. (3) After minimizing the variation of roll gap and applying the new secondary cooling pattern, the occurring frequency of centerline and triangle-zone cracks minimizes to zero.