Preparation and densification of BaTiO3 nanopowder by sol-gel autoigniting synthesis

+ Author Affiliations
  • Corresponding author:

    Fangren Hu    E-mail: Frhu@sina.com

  • Received: 13 November 2001
  • Autoigniting synthesis of gel from Ba(NO3)2, TiO(NO3)2 and C6H8O7·H2O aqueous solution was investigated at an initial temperature of 600℃ and tetragonal BaTiO3 nanopowder with particle size of 80nm was prepared. It is indicated that the specific surface area of the combustion product before and after calcination is 14.74 m2/g and 12.49 m2/g, respectively. The combustion wave is composed of solid phase reaction zone and gaseous phase flame reaction zone. The combustion flame temperature is 1 123 K derived from thermocouple measurement. The characteristics and densification behavior of the sol-gel autoigniting synthesized BaTiO3 nanopowder were investigated.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(261) PDF Downloads(8) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return