Junpin Lin, Yanli Wang, Zhi Lin, and Guoliang Chen, Dynamic recrystallization during hot torsion of Al-4Mg alloy, J. Univ. Sci. Technol. Beijing, 10(2003), No. 2, pp. 45-48.
Cite this article as:
Junpin Lin, Yanli Wang, Zhi Lin, and Guoliang Chen, Dynamic recrystallization during hot torsion of Al-4Mg alloy, J. Univ. Sci. Technol. Beijing, 10(2003), No. 2, pp. 45-48.
Junpin Lin, Yanli Wang, Zhi Lin, and Guoliang Chen, Dynamic recrystallization during hot torsion of Al-4Mg alloy, J. Univ. Sci. Technol. Beijing, 10(2003), No. 2, pp. 45-48.
Citation:
Junpin Lin, Yanli Wang, Zhi Lin, and Guoliang Chen, Dynamic recrystallization during hot torsion of Al-4Mg alloy, J. Univ. Sci. Technol. Beijing, 10(2003), No. 2, pp. 45-48.
Binary Al-4Mg alloy have been deformed by hot torsion at 300-500℃ and strain rates of 0,006-1.587 s-1 to a true strain of 5.5. The specimens were annealed in vacuum for 1.5 h at 500℃ and then water quenched. The study indicates that the dynamic recrystallization occurs during hot torsion of Al-4Mg alloy in a certain range of Z parameter (Zener-Hollmon Parameter), i.e. 19.3 ≤ lnZ ≤ 24.8. Increasing the strain rate at higher deformation temperature or reducing the strain rate at lower deformation temperature accelerates the occurrence of dynamic recrystallization in the alloy.