Microstructure and mechanical propertiesof spray-deposited Al-Si-Fe-Cu-Mg alloy containing Mn

Al-20Si-5Fe-3Cu-1Mg alloy was synthesized by the spray atomization and deposition technique. The microstructure and mechanical properties of the spray deposited hypereutectic Al-Si alloy were studied using optical microscopy, scanning electron microscopy, X-ray diffraction, TEM (Transmission Electron Microscope) and HREM (High-resolution Electron Microscope), DSC (Differential Scanning Calorimetry), microhardness measurement, and tensile tests. The effects of Mn on the microstructural evolution of the high-silicon aluminum alloy after extrusion and heat treatment have been examined. The results show that two kinds of phases, i. e. S (Al2CuMg) and σ(Al5Cu6,Mg2), precipitated from matrix and improved the tensile strength of the alloy efficiently at both the ambient and elevated temperatures (300℃). The tensile test results indicate that the spray-deposited Al-20Si-5Fe-3Cu-1Mg alloy has better strength than the powder metallurgy processed Al-20Si-3Cu-1Mg alloy at elevated temperature.