Biphasic calcium phosphate (BCP) nanopowders were synthesized by using microwave and non-microwave irradiation assisted processes. The synthesized powders were pressed under a pressure of 90 MPa, and then were sintered at 1000^-1200℃ for 1 h. The mechanical properties of the samples were investigated. The formed phases and microstructures were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that the synthesis time was shorter, along with a more homogeneous microstructure, when the microwave irradiation assisted method was applied. The compression strength and the Young's modulus of the samples synthesized with microwave irradiation were about 60 MPa and 3 GPa, but those of the samples synthesized without microwave irradiation were about 30 MPa and 2 GPa, respectively. XRD patterns of the microwave irradiation assisted and non-microwave irradiation assisted nanopowders showed the coexistence of hydroxyapatite (HA) and tricalcium phosphate (TCP) phases in the system.