Abstract: The non-carbothermic zinc pyrometallurgical processing of electric arc furnace (EAF) dust was investigated on a laboratory scale. The main objective of this process was to convert highly stable zinc ferrite (ZnFe₂O₄), which accounts for more than half of total zinc in the EAF dust, into ZnO and Ca₂Fe₂O₅ by CaO addition. The EAF dust was mixed with CaO powder in various ratios, pressed into pellets, and heated in a muffle furnace in air at temperatures ranging from 700 to 1100℃ for a predetermined holding time. All ZnFe₂O₄ was transformed into ZnO and Ca₂Fe₂O₅ at a minimum temperature of 900℃ within 1 h when sufficient CaO to achieve a Ca/Fe molar ratio of 1.1 was added. However, at higher temperatures, excess CaO beyond the stoichiometric ratio was required because it was consumed by reactions leading to the formation of compounds other than ZnFe₂O₄. The evaporation of halides and heavy metals in the EAF dust was also studied. These components could be preferentially volatilized into the gas phase at 1100℃ when CaO was added.