Abstract: To investigate the flow of primary slag bearing TiO₂ in the cohesive zone of blast furnaces,experiments were carried out based on the laboratory-scale packed bed systems.It is concluded that the initial temperature of slag dripping increases with decreasing FeO content and increasing TiO₂ content.The slag holdup decreases when the FeO content is in the range of 5wt%-10wt%,whereas it increases when the FeO content exceeds 10wt%.Meanwhile,the slag holdup decreases when the TiO₂ content increases from 5wt% to 10wt% but increases when the TiO₂ content exceeds 10wt%.Moreover,slag/coke interface analysis shows that the reaction between FeO and TiO₂ occurs between the slag and the coke.The slag/coke interface is divided into three layers:slag layer,iron-rich layer,and coke layer.TiO₂ in the slag is reduced by carbon,and the generated Ti diffuses into iron.