Abstract: The oxidation behavior of a nickel-based superalloy at 1000℃ in air was investigated through X-ray diffraction, scanning electron microscopy, and energy-dispersive spectroscopy analysis. A series of oxides, including external oxide scales (Cr₂O₃, (TiO₂ + MnCr₂O₄)) and internal oxides (Al₂O₃,TiN), were formed on the surface or sub-surface of the substrate at 1000℃ in experimental still air. The oxidation resistance of the alloy was dependent on the stability of the surface oxide layer. The continuity and density of the protective Cr₂O₃ scale were affected by minor alloying elements such as Ti and Mn. The outermost oxide scale was composed of TiO₂ rutile and MnCr₂O₄ spinel, and the growth of TiO₂ particles was controlled by the outer diffusion of Ti ions through the pre-existing oxide layer. Severe internal oxidation occurred beneath the external oxide scale, consuming Al and Ti of the strength phase γ' (Ni₃(Al,Ti)) and thereby severely deteriorating the surface mechanical properties. The depth of the internal oxidation region was approximately 35 μm after exposure to experimental air at 1000℃ for 80 h.