Vinayak Dakre, D. R. Peshwe, S. U. Pathak, and Ajay Likhite, Effect of austenitization temperature on microstructure and mechanical properties of low-carbon-equivalent carbidic austempered ductile iron, Int. J. Miner. Metall. Mater., 25(2018), No. 7, pp. 770-778. https://doi.org/10.1007/s12613-018-1625-4
Cite this article as:
Vinayak Dakre, D. R. Peshwe, S. U. Pathak, and Ajay Likhite, Effect of austenitization temperature on microstructure and mechanical properties of low-carbon-equivalent carbidic austempered ductile iron, Int. J. Miner. Metall. Mater., 25(2018), No. 7, pp. 770-778. https://doi.org/10.1007/s12613-018-1625-4
引用本文 PDF XML SpringerLink
研究论文

Effect of austenitization temperature on microstructure and mechanical properties of low-carbon-equivalent carbidic austempered ductile iron

  • 通讯作者:

    Vinayak Dakre    E-mail: vinayakdakre2007@gmail.com

  • The wear resistances of austempered ductile iron (ADI) were improved through introduction of a new phase (carbide) into the matrix by addition of chromium. In the present investigation, low-carbon-equivalent ductile iron (LCEDI) (CE=3.06%, and CE represents carbon-equivalent) with 2.42% chromium was selected. LCEDI was austenitized at two different temperatures (900 and 975℃) and soaked for 1 h and then quenched in a salt bath at 325℃ for 0 to 10 h. Samples were analyzed using optical microscopy and X-ray diffraction. Wear tests were carried out on a pin-on-disk-type machine. The effect of austenization temperature on the wear resistance, impact strength, and the microstructure was evaluated. A structure–property correlation based on the observations is established.
  • Research Article

    Effect of austenitization temperature on microstructure and mechanical properties of low-carbon-equivalent carbidic austempered ductile iron

    + Author Affiliations
    • The wear resistances of austempered ductile iron (ADI) were improved through introduction of a new phase (carbide) into the matrix by addition of chromium. In the present investigation, low-carbon-equivalent ductile iron (LCEDI) (CE=3.06%, and CE represents carbon-equivalent) with 2.42% chromium was selected. LCEDI was austenitized at two different temperatures (900 and 975℃) and soaked for 1 h and then quenched in a salt bath at 325℃ for 0 to 10 h. Samples were analyzed using optical microscopy and X-ray diffraction. Wear tests were carried out on a pin-on-disk-type machine. The effect of austenization temperature on the wear resistance, impact strength, and the microstructure was evaluated. A structure–property correlation based on the observations is established.
    • loading
    • [1]
      Y. Tanaka and H. Kage, Development and application of austempered spheroidal graphite cast iron, Mater. Trans. JIM, 33(1992), No. 6, p. 543.
      [2]
      Y.S. Lerner and G.R. Kingsbury, Wear resistance properties of austempered ductile iron, J. Mater. Eng. Perform., 7(1998), No. 1, p. 48.
      [3]
      P. Shanmugam, P.P. Rao, K.R. Udupa, and N. Venkataraman, Effect of microstructure on the fatigue strength of an austempered ductile iron, J. Mater. Sci., 29(1994), No. 18, p. 4933.
      [4]
      L. Bartosiewicz, A.R. Krause, F.A. Alberts, I. Singh, and S.K. Putatunda, Influence of microstructure on high cycle fatigue behavior of austempered ductile cast iron, Mater.Charact., 30(1993), No. 4, p. 221.
      [5]
      J.L. Garin and R.L. Mannheim, Strain-induced martensite in ADI alloys, J. Mater. Process. Technol., 143-144(2003), p. 347.
      [6]
      S. Balos, I. Radisavljevic, D. Rajnovic, M. Dramicanin, S. Tabakovic, O. Eric-Cekic, and L. Sidjanin, Geometry, mechanical and ballistic properties of ADI material perforated plates, Mater. Des., 83(2015), p. 66.
      [7]
      R.C. Dommarco, K.J. Kozaczek, P.C. Bastias, G.T. Hahn, and C.A. Rubin, Residual stresses and retained austenite evolution in SAE 52100 steel under non-ideal rolling contact loading, Wear, 257(2004), No. 11, p. 1081.
      [8]
      J. Zimba, D.J. Simbi, and E. Navara, Austempered ductile iron: an alternative material for earth moving components, Cem. Concr. Compos., 25(2003), No. 6, p. 643.
      [9]
      L.Y. Fang and C.R. Loper Jr, Feasibility of the production of a low-cabon equivalent spheroidal graphite cast iron: a review of the literature, Am. Foundry Soc. Trans., 1991, p.313.
      [10]
      A. Likhite, D.R. Peshwe, and S.U. Pathak, Effect of graphite morphology on modulus of elasticity of low carbon equivalent ductile iron, Trans. Indian Inst. Met., 61(2008), No. 6, p. 497.
      [11]
      P. Parhad, S. Umale, A. Likhite, and J. Bhatt, Characterization of inoculated low carbon equivalent iron at lower austempering temperature, Trans. Indian Inst. Met., 65(2012), No. 5, p. 449.
      [12]
      A. Likhite, D.R. Peshwe, and S.U. Pathak, Development of austempered inoculated low carbon equivalent irons, Indian Foundry J., 57(2011), No. 6, p. 23.
      [13]
      S. Umale, A. Likhite, D.R. Peshwe, and S.U. Pathak, Wear characteristics of low carbon equivalent austempered ductile iron (ADI), Indian Foundry J., 60(2014), No. 9, p. 28.
      [14]
      K.L. Hayrynen and K.R. Brandenberg, Carbidic austempered ductile iron (CADI)—the new wear material, Am. Foundry Soc. Trans., 111(2003), p. 845.
      [15]
      J.H. Liu, G.L. Li, X.B. Zhao, X.Y. Hao, and J.J. Zhang, Effect of austempering temperature on microstructure and properties of carbidic austempered ductile iron, Adv. Mater. Res., 284-286(2011), p. 1085.
      [16]
      S. Laino, J.A. Sikora, and R.C. Dommarco, Development of wear resistant carbidic austempered ductile iron (CADI), Wear, 265(2008), No. 1-2, p. 1.
      [17]
      L. Bartosiewicz, I. Singh, F.A. Alberts, A.R. Krause, and S.K. Putatunda, The influence of chromium on mechanical properties of austempered ductile cast iron, J. Mater. Eng. Perform., 4(1995), No. 1, p. 90.
      [18]
      C. Suryanarayana and M. Grant Norton, X-ray Diffraction: A Practical Approach, Plenum Press, New York and London, 1998, p. 153, 223.
      [19]
      C.S. Roberts, Effect of carbon on the volume fractions and lattice parameters of retained austenite and martensite, JOM, 5(1953), No. 2, p. 203.
      [20]
      B.D. Cullity, Elements of X-Ray Diffraction, Addison-Wesley, Reading, USA, 1978, p.102.
      [21]
      P. Parhad, A. Likhite, J. Bhatt, and D. Peshwe, The effect of cutting speed and depth of cut on surface roughness during machining of austempered ductile iron, Trans. Indian Inst. Met., 68(2015), No. 1, p. 99.
      [22]
      H.O. Pierson, Handbook of Refractory Carbides and Nitrides: Properties, Characteristics, Processing and Applications, William Andrew, 1996, p. 139.
      [23]
      T.N. Rouns and K.B. Rundman, Constitution of austempered ductile iron and the kinetics of austempering, Am. Foundry Soc. Trans., 95(1987), p. 851.
      [24]
      R. Elliott, Cast Iron Technology, Butterworth-Heinemann, Oxford, 1988, p. 142.
      [25]
      C.H. Hsu and S.C. Lee, High strength high toughness compacted graphite cast iron, Mater. Sci. Technol., 11(1995), p. 765.
      [26]
      U. Batra, S. Ray, and S.R. Prabhakar, Impact properties of copper-alloyed and nickel-copper alloyed ADI, J. Mater. Eng. Perform., 16(2007), No. 4, p. 485.
      [27]
      U.R. Kumari and P.P. Rao, Study of wear behaviour of austempered ductile iron, J. Mater. Sci., 44(2009), p. 1082.
      [28]
      J.H. Yang and S.K. Putatunda, Effect of microstructure on abrasion wear behavior of austempered ductile cast iron (ADI) processed by a novel two-step austempering process, Mater. Sci. Eng. A, 406(2005), No. 1-2, p. 217.

    Catalog


    • /

      返回文章
      返回