Abstract: The Ni samples were electroformed from additive-free (AF) and saccharin-containing (SC) sulfamate solutions, respectively. In situ backscattered electron (BSE) imaging, electron backscatter diffraction (EBSD), and electron-probe microanalysis (EPMA) were used to investigate the effect of annealing on the deformation behaviors of the AF and SC samples. The results indicate that columnar grains of the as-deposited AF sample had an approximated average width of 3 μm and an approximated aspect ratio of 8. The average width of columnar grains of the as-deposited SC sample was reduced to approximately 400 nm by the addition of saccharin to the electrolyte. A few very-large grains distributed in the matrix of the SC sample after annealing. No direct evidence indicated that S segregated at the grain boundaries before or after annealing. The average value of the total elongations of the SC samples decreased from 16% to 6% after annealing, whereas that of the AF samples increased from 18% to 50%. The dislocation recovery in grain-boundary areas of the annealed AF sample was reduced, which contributed to the appearance of microvoids at the triple junctions. The incompatibility deformation between very-large grains and fine grains contributed to the brittle fracture behavior of the annealed SC Ni.