Abstract: An efficient approach for lead extraction from waste funnel glass through the lead smelting process has been proposed. To clarify the effect of funnel glass addition on the degradation of magnesia-chromite refractories by ZnO-containing fayalite slag, the corrosion behavior of magnesia-chromite refractories in lead smelting slags with different funnel glass additions from 0wt% to 40wt% was tested. Scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) was used to acquire the microstructural information of the worn refractory samples. Experimental results showed that the corrosion of magnesia-chromite refractory consisted predominantly of the dissolution of MgO into slag. ZnO and FeO reacted with periclase and chromite to form (Zn,Fe,Mg)O solid solution and (Zn,Fe,Mg)(Fe,Al,Cr)₂O₄ spinel, respectively. With the addition of funnel glass, the solubility of MgO increased whereas ZnO levels remained stable, thereby resulting in a reduced Mg content and an elevated Zn and Fe content in the (Zn,Fe,Mg)O solid solution and the (Zn,Fe,Mg)(Fe,Al,Cr)₂O₄ spinel. Considering the stability of the (Zn,Fe,Mg)O solid solution layer and the penetration depth of the slag, the optimal funnel glass addition for lead smelting was found to be 20wt%.