Zhenmin Wang, Yuan Fang, Junjie Qi, Yue Zhang, Yan Yu,  and Jianchun Wu, Microstructure analysis of AISI 304 stainless steel produced by twin-roll thin strip casting process, J. Univ. Sci. Technol. Beijing, 14(2007), No. 5, pp. 420-424. https://doi.org/10.1016/S1005-8850(07)60083-8
Cite this article as:
Zhenmin Wang, Yuan Fang, Junjie Qi, Yue Zhang, Yan Yu,  and Jianchun Wu, Microstructure analysis of AISI 304 stainless steel produced by twin-roll thin strip casting process, J. Univ. Sci. Technol. Beijing, 14(2007), No. 5, pp. 420-424. https://doi.org/10.1016/S1005-8850(07)60083-8
引用本文 PDF XML SpringerLink
Materials

Microstructure analysis of AISI 304 stainless steel produced by twin-roll thin strip casting process

  • 通讯作者:

    Yue Zhang    E-mail: yuezhang@ustb.edu.cn

  • The microstructure of AISI 304 austenlte stainless steel fabricated by the thin strip casting process were investigated using optical microscope, scanning electron microscope (SEM), transmission electron microscope (TEM), and X-ray diffraction (XRD). The microstructures of the casting strips show a duplex structure consisting of delta ferrite and austenite. The volume fraction of the delta ferrite is about 9.74vo1% at the center and 6.77vo1% at the surface of the casting thin strip, in vermicular and hand shapes. On account of rapid cooling and solidification in the continuous casting process, many kinds of inclusions and precipitates have been found. Most of the inclusions and precipitates are spherical complex compounds consisting of oxides, such as, SiO2, MnO, Al2O3, Cr2O3, and FeO or their multiplicity oxides of MnO·Al2O3, 2FeO·SiO2, and 2MnO·SiO2. Many defects including dislocations and stacking faults have also formed during the rapid cooling and solidification process, which is helpful to improve the mechanical properties of the casting strips.
  • Materials

    Microstructure analysis of AISI 304 stainless steel produced by twin-roll thin strip casting process

    + Author Affiliations
    • The microstructure of AISI 304 austenlte stainless steel fabricated by the thin strip casting process were investigated using optical microscope, scanning electron microscope (SEM), transmission electron microscope (TEM), and X-ray diffraction (XRD). The microstructures of the casting strips show a duplex structure consisting of delta ferrite and austenite. The volume fraction of the delta ferrite is about 9.74vo1% at the center and 6.77vo1% at the surface of the casting thin strip, in vermicular and hand shapes. On account of rapid cooling and solidification in the continuous casting process, many kinds of inclusions and precipitates have been found. Most of the inclusions and precipitates are spherical complex compounds consisting of oxides, such as, SiO2, MnO, Al2O3, Cr2O3, and FeO or their multiplicity oxides of MnO·Al2O3, 2FeO·SiO2, and 2MnO·SiO2. Many defects including dislocations and stacking faults have also formed during the rapid cooling and solidification process, which is helpful to improve the mechanical properties of the casting strips.