Xiaoyuan Dai, Changqing Xia, Xiaomin Peng, and Ke Ma, Structure and properties of an ultra-high strength 7xxx aluminum alloy contained Sc and Zr, J. Univ. Sci. Technol. Beijing, 15(2008), No. 3, pp. 276-279. https://doi.org/10.1016/S1005-8850(08)60052-3
Cite this article as:
Xiaoyuan Dai, Changqing Xia, Xiaomin Peng, and Ke Ma, Structure and properties of an ultra-high strength 7xxx aluminum alloy contained Sc and Zr, J. Univ. Sci. Technol. Beijing, 15(2008), No. 3, pp. 276-279. https://doi.org/10.1016/S1005-8850(08)60052-3
Xiaoyuan Dai, Changqing Xia, Xiaomin Peng, and Ke Ma, Structure and properties of an ultra-high strength 7xxx aluminum alloy contained Sc and Zr, J. Univ. Sci. Technol. Beijing, 15(2008), No. 3, pp. 276-279. https://doi.org/10.1016/S1005-8850(08)60052-3
Citation:
Xiaoyuan Dai, Changqing Xia, Xiaomin Peng, and Ke Ma, Structure and properties of an ultra-high strength 7xxx aluminum alloy contained Sc and Zr, J. Univ. Sci. Technol. Beijing, 15(2008), No. 3, pp. 276-279. https://doi.org/10.1016/S1005-8850(08)60052-3
An ultra-high strength aluminum alloy was produced by casting and then extruded to rods. The effect of heat treatment on the microstructure and mechanical properties of the alloy was investigated. After single ageing (120℃, 24 h), the tensile strength was 812.4 MPa and the elongation was 6.2%. After retrogression reaging (RRA), the tensile strength was 751.2 MPa and the elongation was 6.4%. The strengthening mechanism is considered as fine grain strengthening, substructure strengthening and dispersion strengthening by Al3(Sc, Zr).
An ultra-high strength aluminum alloy was produced by casting and then extruded to rods. The effect of heat treatment on the microstructure and mechanical properties of the alloy was investigated. After single ageing (120℃, 24 h), the tensile strength was 812.4 MPa and the elongation was 6.2%. After retrogression reaging (RRA), the tensile strength was 751.2 MPa and the elongation was 6.4%. The strengthening mechanism is considered as fine grain strengthening, substructure strengthening and dispersion strengthening by Al3(Sc, Zr).