Abstract: A predominance area diagram for the Zr-Si-C-O system at 1773 K was plotted according to correlative thermodynamic data. β-SiC/ZrO₂ composites were prepared based on the phase diagram by carbothermal reduction of zircon (ZrSiO₄) in argon atmosphere. Zircon and carbon black were mixed according to the C/ZrSiO₄ mass ratio of 0.2, and with 0, 1wt% and 2wt% extra addition of La₂O₃. Phase evolution of the mixture was investigated at 1723-1803 K by X-ray powder diffraction, and the microstructure of the product prepared at 1803 K for 4 h was examined by scanning electronic microscope. The results show that the decomposition of ZrSiO₄ and the formation of β-SIC can be promoted by increasing the heating temperature and adding La₂O₃. The β-SiC/ZrO₂ composites can be prepared at 1803 K for 4 h in a mixture of zircon, carbon black and La₂O₃, and the contents of β-SIC and m-ZrO₂ in the product sample with 2wt% La₂O₃ reach the highest values of 10.8wt% and 89.2wt%, respectively. The crystal size of the products is about 200 nm.