留言板

尊敬的读者、作者、审稿人, 关于本刊的投稿、审稿、编辑和出版的任何问题, 您可以本页添加留言。我们将尽快给您答复。谢谢您的支持!

姓名
邮箱
手机号码
标题
留言内容
验证码
Volume 4 Issue 4
Dec.  1997
数据统计

分享

计量
  • 文章访问数:  316
  • HTML全文浏览量:  116
  • PDF下载量:  11
  • 被引次数: 0
WANG Xinhua, WANG Wenjun, WU Dongmei, CHANG Bo, LIU Xinyu, ZHANG Li,  and YE Jinwei, Preventing Occurrence of Transverse Corner Cracks on Nb, V and Ti Microalloying Steel CC Slabs, J. Univ. Sci. Technol. Beijing, 4(1997), No. 4, pp. 5-9.
Cite this article as:
WANG Xinhua, WANG Wenjun, WU Dongmei, CHANG Bo, LIU Xinyu, ZHANG Li,  and YE Jinwei, Preventing Occurrence of Transverse Corner Cracks on Nb, V and Ti Microalloying Steel CC Slabs, J. Univ. Sci. Technol. Beijing, 4(1997), No. 4, pp. 5-9.
引用本文 PDF XML SpringerLink

Preventing Occurrence of Transverse Corner Cracks on Nb, V and Ti Microalloying Steel CC Slabs

  • Based on their hot ductilities, Nb, V and Ti microalloying steels can be classified into two groups. The first group includes steels with lower carbon content (≤0.10%). Ductilities of steels of this group recover and rise with decreasing temperature when temperature lowers to below 825℃. Another group includes steels which contain more carbon (>0.12%) or contain more Nb and V. The low ductility temperature Region Ⅲ for steels of mis group extends to temperature as low as 725℃. The occurrence of the transverse corner cracks of the Nb, V and Ti microalloying steel CC slabs has be considerably decreased by stabilizing casting speed, increasing mold steel level automatic control ratio,enhancing caster segment radial alignment and adopting proper secondary cooling patterns to make slab corner temperature at straightening out off the low ductility temperature region.
  • Preventing Occurrence of Transverse Corner Cracks on Nb, V and Ti Microalloying Steel CC Slabs

    + Author Affiliations
    • Based on their hot ductilities, Nb, V and Ti microalloying steels can be classified into two groups. The first group includes steels with lower carbon content (≤0.10%). Ductilities of steels of this group recover and rise with decreasing temperature when temperature lowers to below 825℃. Another group includes steels which contain more carbon (>0.12%) or contain more Nb and V. The low ductility temperature Region Ⅲ for steels of mis group extends to temperature as low as 725℃. The occurrence of the transverse corner cracks of the Nb, V and Ti microalloying steel CC slabs has be considerably decreased by stabilizing casting speed, increasing mold steel level automatic control ratio,enhancing caster segment radial alignment and adopting proper secondary cooling patterns to make slab corner temperature at straightening out off the low ductility temperature region.