A new kind of sintering process, combined sintering process. i.e. vacuum sintering plus hot isolate pressure sintering (HIP), was introduced for producing ultrafine WC-10% Co (mass fraction. so as the follows) cemented carbides. The effects of some processing parameters on the microstructure and mechanical properties of the obtained cemented carbides were studied. The results show that the rapid shrinkage and the pronounced densification of tile cemented carbides took place during the vacuum sintering stage, which is intinaately correlated with the local liquid sintering occurred during this earl} sintering stage for the high surface activity of ultrafine WC-Co powder. The way of high pressure imposing. isothermal treatment cycle during ac.acuum sintering and HIP sintering stage directly influence the densitication of compacts and the mechanical properties of the produced WC-10%Co cemented carbides.
A new kind of sintering process, combined sintering process. i.e. vacuum sintering plus hot isolate pressure sintering (HIP), was introduced for producing ultrafine WC-10% Co (mass fraction. so as the follows) cemented carbides. The effects of some processing parameters on the microstructure and mechanical properties of the obtained cemented carbides were studied. The results show that the rapid shrinkage and the pronounced densification of tile cemented carbides took place during the vacuum sintering stage, which is intinaately correlated with the local liquid sintering occurred during this earl} sintering stage for the high surface activity of ultrafine WC-Co powder. The way of high pressure imposing. isothermal treatment cycle during ac.acuum sintering and HIP sintering stage directly influence the densitication of compacts and the mechanical properties of the produced WC-10%Co cemented carbides.
下载: