The bonding of solid steel to liquid aluminum was conducted using rapid solidification. The influence of diffusion time on interfacial shear strength was studied. The results show that when the temperature of aluminum liquid is 700℃ and the preheat temperature of steel plate is 250℃, the relationship between diffusion time (t) and interfacial shear strength (σ) is (σ=15.1+8.14t(037t2 +0.005t3, and the maximum interfacial shear strength is 71.1 MPa.
Influence of diffusion time on property of steel-aluminum solid to liquid bonding
Abstract:
The bonding of solid steel to liquid aluminum was conducted using rapid solidification. The influence of diffusion time on interfacial shear strength was studied. The results show that when the temperature of aluminum liquid is 700℃ and the preheat temperature of steel plate is 250℃, the relationship between diffusion time (t) and interfacial shear strength (σ) is (σ=15.1+8.14t(037t2 +0.005t3, and the maximum interfacial shear strength is 71.1 MPa.
下载: