Influence of aluminum solid fraction on property of steel-mushy aluminum bonding plate

摘要: The interfacial shear property of steel-mushy aluminum bonding plate was studied, and the relationship between aluminum solid fraction and the interfacial shear strength of bonding plate was determined. The results showed that when aluminum solid fraction is 34.3 %, the maximum interfacial shear strength of bonding plate is 71.0 MPa.

 

Influence of aluminum solid fraction on property of steel-mushy aluminum bonding plate

Abstract: The interfacial shear property of steel-mushy aluminum bonding plate was studied, and the relationship between aluminum solid fraction and the interfacial shear strength of bonding plate was determined. The results showed that when aluminum solid fraction is 34.3 %, the maximum interfacial shear strength of bonding plate is 71.0 MPa.

 