Fluidization behavior and reduction kinetics of pre-oxidized magnetite-based iron ore in a hydrogen-induced fluidized bed

+ Author Affiliations
  • Received: 28 January 2022Revised: 25 April 2022Accepted: 28 April 2022Available online: 29 April 2022
  • The influence of different pre-oxidation temperature and pre-oxidation degree on the reduction and fluidization behaviors of magnetite-based iron ore was investigated in a hydrogen-induced fluidized bed. The raw magnetite-based iron ore was pre-oxidized at 800 and 1000 °C for a certain time to reach a partly oxidation and deeply oxidation state. The structure and morphology of the reduced particles were analyzed via optical microscope and scanning electron microscopy (SEM). The reaction kinetic mechanism was determined based on the double-logarithm analysis. The results indicate that the materials with higher oxidation temperature and wider particle size range showed better fluidization behaviors. While lower oxidation temperature was more beneficial for the reduction rate, especially in the later reduction stage. The pre-oxidation degree shows no obvious influence on the fluidization and reduction behaviors. The reduction progress can be divided into three stages. The reduction mechanism was discussed combing the surface morphology and phase structure.

  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(104) PDF Downloads(16) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return