High corrosion and wear resistant electroless Ni-P gradient coatings on aviation aluminum alloy parts

+ Author Affiliations
  • Received: 1 February 2023Revised: 25 April 2023Accepted: 5 June 2023Available online: 6 June 2023
  • A Ni-P alloy gradient coating consisting of multiple electroless Ni-P layers with various phosphorus content was prepared on the aviation aluminum alloy. Several characterization and electrochemical techniques were used to characterize the different Ni-P coatings’ morphologies, phase structures, elemental compositions, and corrosion protection. The gradient coating showed good adhesion, and high corrosion and wear resistance, enabling the application of aluminum alloy in harsh environments. The results showed that the double zinc immersion was vital in obtaining excellent adhesion (81.2 N). The optimal coating was not peeled and shredded even after bending tests with angles higher than 90° and was not corroded visually after 500 h of neutral salt spray test at 35 ℃. The high corrosion resistance was attributed to the misaligning of these micro defects in the three different nickel alloy layers and the amorphous structure of the high P content in the outer layer. These findings guide the exploration of functional gradient coatings that meet the high application requirement of aluminum alloy parts in complicated and harsh aviation environments.

  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(94) PDF Downloads(13) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return