Chun-lei Zhu, Qing Wang, Jie Zhang, Ying-min Wang,  and Chuang Dong, Formation and corrosion properties of Fe-based bulk metallic glasses, Int. J. Miner. Metall. Mater., 17(2010), No. 3, pp. 323-326. https://doi.org/10.1007/s12613-010-0312-x
Cite this article as:
Chun-lei Zhu, Qing Wang, Jie Zhang, Ying-min Wang,  and Chuang Dong, Formation and corrosion properties of Fe-based bulk metallic glasses, Int. J. Miner. Metall. Mater., 17(2010), No. 3, pp. 323-326. https://doi.org/10.1007/s12613-010-0312-x

Formation and corrosion properties of Fe-based bulk metallic glasses

+ Author Affiliations
  • Corresponding author:

    Chuang Dong    E-mail: dong@dlut.edu.cn

  • Received: 8 June 2009Revised: 17 July 2009Accepted: 25 July 2009
  • Bulk metallic glass (BMG) formation was explored in the Fe-B-Si-Nb alloy system though combined use of the atomic cluster line approach and the minor alloying strategy. The basic ternary compositions in the Fe-B-Si system were determined by the intersection points of two cluster lines, namely, Fe-B cluster to Si and Fe-Si cluster to B. 3at%–4at% Nb was added to the quaternary Fe-B-Si-Nb alloy. The casting experiments revealed that good glass-forming ability (GFA) occurred at the (Fe73.4Si8.2B18.4)96Nb4 composition, and 3-mm diameter BMG samples were made. The glass transition temperature (Tg), crystallization temperature (Tx), and supercooled liquid region (ΔTx=Tx-Tg) of this BMG were measured to be 866, 889, and 23 K, respectively. The BMG shows a high Vickers hardness of about Hv 1164, a Young’s modulus of 180 GPa, and a good corrosion resistance in the solutions of 1 mol/L HCl and 3wt% NaCl.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(230) PDF Downloads(15) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return