Effect of aluminum oxide on the compressive strength of pellets

Analytical-reagent-grade Al₂O₃ was added to magnetite ore during the process of pelletizing, and the methods of mercury intrusion, scanning electron microscopy, and image processing were used to investigate the effect of Al₂O₃ on the compressive strength of the pellets. The results showed that, as the Al₂O₃ content increased, the compressive strength of the pellets increased slightly and then decreased gradually. When a small amount of Al₂O₃ was added to the pellets, the Al₂O₃ combined with fayalite (2FeO·SiO₂) and the aluminosilicate (2FeO·2Al₂O₃·5SiO₂) was generated, which releases some iron oxide and reduces the inhibition of fayalite to the solid phase of consolidation. When Al₂O₃ increased sequentially, high melting point of Al₂O₃ particles hinder the oxidation of Fe₃O₄ and the recrystallization of Fe2O3, making the internal porosity of the pellets increase, which leads to the decrease in compressive strength of the pellets.