Tao Yang, Ya-peng Zheng, Kuo-Chih Chou, and Xin-mei Hou, Tunable fabrication of single-crystalline CsPbI3 nanobelts and their application as photodetectors, Int. J. Miner. Metall. Mater., 28(2021), No. 6, pp. 1030-1037. https://doi.org/10.1007/s12613-020-2173-2
Cite this article as:
Tao Yang, Ya-peng Zheng, Kuo-Chih Chou, and Xin-mei Hou, Tunable fabrication of single-crystalline CsPbI3 nanobelts and their application as photodetectors, Int. J. Miner. Metall. Mater., 28(2021), No. 6, pp. 1030-1037. https://doi.org/10.1007/s12613-020-2173-2
Research Article

Tunable fabrication of single-crystalline CsPbI3 nanobelts and their application as photodetectors

+ Author Affiliations
  • Corresponding author:

    Xin-mei Hou    E-mail: houxinmeiustb@ustb.edu.cn

  • Received: 20 June 2020Revised: 20 August 2020Accepted: 25 August 2020Available online: 27 August 2020
  • Lead halide perovskites have received increasing attention recently as a candidate material in various optoelectronic areas because of their high performance as light absorbers. Herein, we report the growth of CsPbI3 nanobelts via a solution process. A single-crystalline CsPbI3 nanobelt with uniform morphology can be achieved by controlling the amount of PbI2. A single-crystalline CsPbI3 nanobelt possesses a mean width, length, and thickness of 100 nm, 5 µm, and 20 nm, respectively. In this work, photodetectors (PDs) based on individual CsPbI3 nanobelts are constructed and found to perform well with an external quantum efficiency and responsivity of 2.39 × 105% and 770 A/W, respectively. The PDs also show a high detectivity of up to 3.12 × 1012 Jones, which is at par with that of Si PDs. The PDs developed in this work exhibit great promise in various optoelectronic nanodevices.
  • loading
  • [1]
    N.J. Jeon, J.H. Noh, W.S. Yang, Y.C. Kim, S. Ryu, J. Seo, and S.I. Seok, Compositional engineering of perovskite materials for high-performance solar cells, Nature, 517(2015), No. 7535, p. 476. doi: 10.1038/nature14133
    L. Protesescu, S. Yakunin, M.I. Bodnarchuk, F. Krieg, R. Caputo, C.H. Hendon, R.X. Yang, A. Walsh, and M.V. Kovalenko, Nanocrystals of cesium lead halide perovskites (CsPbX3, X = Cl, Br, and I): Novel optoelectronic materials showing bright emission with wide color gamut, Nano Lett., 15(2015), No. 6, p. 3692. doi: 10.1021/nl5048779
    B. Conings, J. Drijkoningen, N. Gauquelin, A. Babayigit, J. D'Haen, L. D'Olieslaeger, A. Ethirajan, J. Verbeeck, J. Manca, E. Mosconi, F. de Angelis, and H.G. Boyen, Intrinsic thermal instability of methylammonium lead trihalide perovskite, Adv. Energy Mater., 5(2015), No. 15, art. No. 1500477. doi: 10.1002/aenm.201500477
    J. Yang, B.D. Siempelkamp, D. Liu, and T.L. Kelly, Investigation of CH3NH3PbI3 degradation rates and mechanisms in controlled humidity environments using in situ techniques, ACS Nano, 9(2015), No. 2, p. 1955. doi: 10.1021/nn506864k
    P. Liu, X.X. He, J.H. Ren, Q. Liao, J.N. Yao, and H.B. Fu, Organic–inorganic hybrid perovskite nanowire laser arrays, ACS Nano, 11(2017), No. 6, p. 5766. doi: 10.1021/acsnano.7b01351
    M.I. Saidaminov, M.A. Haque, M. Savoie, A.L. Abdelhady, N. Cho, I. Dursun, U. Buttner, E. Alarousu, T. Wu, and O.M. Bakr, Perovskite photodetectors operating in both narrowband and broadband regimes, Adv. Mater., 28(2016), No. 37, p. 8144. doi: 10.1002/adma.201601235
    T. Yang, Y.P. Zheng, Z.T. Du, W.N. Liu, Z.B. Yang, F.M. Gao, L. Wang, K.C. Chou, X.M. Hou, and W.Y. Yang, Superior photodetectors based on all-inorganic perovskite CsPbI3 nanorods with ultrafast response and high stability, ACS Nano, 12(2018), No. 2, p. 1611. doi: 10.1021/acsnano.7b08201
    L. Meng, E.P. Yao, Z.R. Hong, H.J. Chen, P.Y. Sun, Z.L. Yang, G. Li, and Y. Yang, Pure formamidinium-based perovskite light-emitting diodes with high efficiency and low driving voltage, Adv. Mater., 29(2017), No. 4, art. No. 1603826. doi: 10.1002/adma.201603826
    M. Saliba, T. Matsui, K. Domanski, J.Y. Seo, A. Ummadisingu, S.M. Zakeeruddin, J.P. Correa-Baena, W.R. Tress, A. Abate, A. Hagfeldt, and M. Gratzel, Incorporation of rubidium cations into perovskite solar cells improves photovoltaic performance, Science, 354(2016), No. 6309, p. 206. doi: 10.1126/science.aah5557
    D.W. Zhao, Y. Yu, C.L. Wang, W.Q. Liao, N. Shrestha, C.R. Grice, A.J. Cimaroli, L. Guan, R.J. Ellingson, K. Zhu, X.Z. Zhao, R.G. Xiong, and Y.F. Yan, Low-bandgap mixed tin–lead iodide perovskite absorbers with long carrier lifetimes for all-perovskite tandem solar cells, Nat. Energy, 2(2017), No. 4, art. No. 17018. doi: 10.1038/nenergy.2017.18
    X.M. Li, D.J. Yu, F. Cao, Y. Gu, Y. Wei, Y. Wu, J.Z. Song, and H.B. Zeng, Healing all-inorganic perovskite films via recyclable dissolution–recyrstallization for compact and smooth carrier channels of optoelectronic devices with high stability, Adv. Funct. Mater., 26(2016), No. 32, p. 5903. doi: 10.1002/adfm.201601571
    M.I. Saidaminov, M.A. Haque, J. Almutlaq, S. Sarmah, X.H. Miao, R. Begum, A.A. Zhumekenov, I. Dursun, N. Cho, B. Murali, O.F. Mohammed, T. Wu, and O.M. Bakr, Inorganic lead halide perovskite single crystals: Phase-selective low-temperature growth, carrier transport properties, and self-powered photodetection, Adv. Opt. Mater., 5(2017), No. 2, art. No. 1600704. doi: 10.1002/adom.201600704
    A. Waleed, M.M. Tavakoli, L.L. Gu, S. Hussain, D.Q. Zhang, S. Poddar, Z.Y. Wang, R.J. Zhang, and Z.Y. Fan, All inorganic cesium lead iodide perovskite nanowires with stabilized cubic phase at room temperature and nanowire array-based photodetectors, Nano Lett., 17(2017), No. 8, p. 4951. doi: 10.1021/acs.nanolett.7b02101
    W.Y. Nie, H. Tsai, R. Asadpour, J.C. Blancon, A.J. Neukirch, G. Gupta, J.J. Crochet, M. Chhowalla, S. Tretiak, M.A. Alam, H.L. Wang, and A.D. Mohite, Solar cells. High-efficiency solution-processed perovskite solar cells with millimeter-scale grains, Science, 347(2015), No. 6221, p. 522. doi: 10.1126/science.aaa0472
    Q.F. Dong, Y.J. Fang, Y.C. Shao, P. Mulligan, J. Qiu, L. Cao, and J.S. Huang, Solar cells. Electron-hole diffusion lengths > 175 μm in solution-grown CH3NH3PbI3 single crystals, Science, 347(2015), No. 6225, p. 967. doi: 10.1126/science.aaa5760
    W. Deng, X.J. Zhang, L.M. Huang, X.Z. Xu, L. Wang, J.C. Wang, Q.X. Shang, S.T. Lee, and J.S. Jie, Aligned single-crystalline perovskite microwire arrays for high-performance flexible image sensors with long-term stability, Adv. Mater., 28(2016), No. 11, p. 2201. doi: 10.1002/adma.201505126
    J. Xing, X.F. Liu, Q. Zhang, S.T. Ha, Y.W. Yuan, C. Shen, T.C. Sum, and Q.H. Xiong, Vapor phase synthesis of organometal halide perovskite nanowires for tunable room-temperature nanolasers, Nano Lett., 15(2015), No. 7, p. 4571. doi: 10.1021/acs.nanolett.5b01166
    H.M. Zhu, Y.P. Fu, F. Meng, X.X. Wu, Z.Z. Gong, Q. Ding, M.V. Gustafsson, M.T. Trinh, S. Jin, and X.Y. Zhu, Lead halide perovskite nanowire lasers with low lasing thresholds and high quality factors, Nat. Mater., 14(2015), No. 6, p. 636. doi: 10.1038/nmat4271
    D.M. Trots and S.V. Myagkota, High-temperature structural evolution of caesium and rubidium triiodoplumbates, J. Phys. Chem. Solids, 69(2008), No. 10, p. 2520. doi: 10.1016/j.jpcs.2008.05.007
    C.K. Møller, Crystal structure and photoconductivity of cæsium plumbohalides, Nature, 182(1958), No. 4647, p. 1436. doi: 10.1038/1821436a0
    P.A. Hu, Z.Z. Wen, L.F. Wang, P.H. Tan, and K. Xiao, Synthesis of few-layer GaSe nanosheets for high performance photodetectors, ACS Nano, 6(2012), No. 7, p. 5988. doi: 10.1021/nn300889c
    L. Ma, W. Hu, Q.L. Zhang, P.Y. Ren, X.J. Zhuang, H. Zhou, J.Y. Xu, H.L. Li, Z.P. Shan, X.X. Wang, L. Liao, H.Q. Xu, and A.L. Pan, Room-temperature near-infrared photodetectors based on single heterojunction nanowires, Nano Lett., 14(2014), No. 2, p. 694. doi: 10.1021/nl403951f
    L.T. Dou, Y. Yang, J.B. You, Z.R. Hong, W.H. Chang, G. Li, and Y. Yang, Solution-processed hybrid perovskite photodetectors with high detectivity, Nat. Commun., 5(2014), art. No. 5404. doi: 10.1038/ncomms6404
    X. Gong, M.H. Tong, Y.J. Xia, W.Z. Cai, J.S. Moon, Y. Cao, G. Yu, C.L. Shieh, B. Nilsson, and A.J. Heeger, High-detectivity polymer photodetectors with spectral response from 300 nm to 1450 nm, Science, 325(2009), No. 5948, p. 1665. doi: 10.1126/science.1176706
    S. Panigrahi and D. Basak, Core-shell TiO2@ZnO nanorods for efficient ultraviolet photodetection, Nanoscale, 3(2011), No. 5, p. 2336. doi: 10.1039/c1nr10064e
    H. Kind, H. Yan, B. Messer, M. Law, and P. Yang, Nanowire ultraviolet photodetectors and optical switches, Adv. Mater., 14(2002), No. 2, p. 158. doi: 10.1002/1521-4095(20020116)14:2<158::AID-ADMA158>3.0.CO;2-W
    C. Soci, A. Zhang, B. Xiang, S.A. Dayeh, D.P.R. Aplin, J. Park, X.Y. Bao, Y.H. Lo, and D. Wang, ZnO nanowire UV photodetectors with high internal gain, Nano Lett., 7(2007), No. 4, p. 1003. doi: 10.1021/nl070111x
    H. Liu, Z.M. Zhang, L.F. Hu, N. Gao, L.W. Sang, M.Y. Liao, R.Z. Ma, F.F. Xu, and X.S. Fang, New UV-A photodetector based on individual potassium niobate nanowires with high performance, Adv. Opt. Mater., 2(2014), No. 8, p. 771. doi: 10.1002/adom.201400176
    X. Hu, X.D. Zhang, L. Liang, J. Bao, S. Li, W.L. Yang, and Y. Xie, High-performance flexible broadband photodetector based on organolead halide perovskite, Adv. Funct. Mater., 24(2014), No. 46, p. 7373. doi: 10.1002/adfm.201402020
    H. Deng, X.K. Yang, D.D. Dong, B. Li, D. Yang, S.J. Yuan, K.K. Qiao, Y.B. Cheng, J. Tang, and H.S. Song, Flexible and semitransparent organolead triiodide perovskite network photodetector arrays with high stability, Nano Lett., 15(2015), No. 12, p. 7963. doi: 10.1021/acs.nanolett.5b03061
    Y.H. Dong, Y. Gu, Y.S. Zou, J.Z. Song, L.M. Xu, J.H. Li, J. Xue, X.M. Li, and H.B. Zeng, Improving all-inorganic perovskite photodetectors by preferred orientation and plasmonic effect, Small, 12(2016), No. 40, p. 5622. doi: 10.1002/smll.201602366
    Y. Li, Z.F. Shi, S. Li, L.Z. Lei, H.F. Ji, D. Wu, T.T. Xu, Y.T. Tian, and X.J. Li, High-performance perovskite photodetectors based on solution-processed all-inorganic CsPbBr3 thin films, J. Mater. Chem. C, 5(2017), No. 33, p. 8355. doi: 10.1039/C7TC02137B
    X.M. Li, D.J. Yu, J. Chen, Y. Wang, F. Cao, Y. Wei, Y. Wu, L. Wang, Y. Zhu, Z.G. Sun, J.P. Ji, Y.L. Shen, H.D. Sun, and H.B. Zeng, Constructing fast carrier tracks into flexible perovskite photodetectors to greatly improve responsivity, ACS Nano, 11(2017), No. 2, p. 2015. doi: 10.1021/acsnano.6b08194
    X.H. Liu, D.J. Yu, F. Cao, X.M. Li, J.P. Ji, J. Chen, X.F. Song, and H.B. Zeng, Low-voltage photodetectors with high responsivity based on solution-processed micrometer-scale all-inorganic perovskite nanoplatelets, Small, 13(2017), No. 25, art. No. 1700364. doi: 10.1002/smll.201700364
    M. Shoaib, X.H. Zhang, X.X. Wang, H. Zhou, T. Xu, X. Wang, X.L. Hu, H.W. Liu, X.P. Fan, W.H. Zheng, T.F. Yang, S.Z. Yang, Q.L. Zhang, X.L. Zhu, L.T. Sun, and A.L. Pan, Directional growth of ultralong CsPbBr3 perovskite nanowires for high-performance photodetectors, J. Am. Chem. Soc., 139(2017), No. 44, p. 15592. doi: 10.1021/jacs.7b08818
  • 加载中


    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Figures(6)  / Tables(1)

    Share Article

    Article Metrics

    Article views (1584) PDF downloads(36) Cited by()
    Proportional views


    DownLoad:  Full-Size Img  PowerPoint