A cluster line approach to finding new Fe-B-Y-Nb-Zr bulk metallic glasses

+ Author Affiliations
  • Corresponding author:

    Chuang Dong    E-mail: dong@dlut.edu.cn

  • Received: 5 June 2006
  • The glass forming ability of the [(Fe12/13Y1/13)100-xBx]96Nb2Zr2 (x=9–26) system was investigated using a series of cluster lines. Three types of clusters, an icosahedron (Fe12Y), a capped Archimedes anti-prism (Fe8B3) and a capped trigonal prism (Fe9B), as well as a binary eutectic (Fe83B17) were considered. Bulk glassy alloy rods of 3 mm in diameter were synthesized using a copper mold suction-casting method. The glass transition temperature was observed for all samples in the boron range of 15.9at%-25.7at%, with the alloy at 15.9at% of boron having the best thermal properties. The ferrous-based bulk metallic glasses (BMG) obtained have high reduced glass transition temperatures with the maximum reaching 0.63 and large supercooled liquid regions with the maximum reaching 111 K. Magnetic testing revealed a large value of coercive force and remanent magnetization, being 11 kA/m and 0.1 T, respectively.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(339) PDF Downloads(6) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return