Zhenhua Li and Xianhua Cheng, Deformation temperature and postdeformation annealing effects on severely deformed TiNi alloy by equal channel angular extrusion, J. Univ. Sci. Technol. Beijing, 14(2007), No. 6, pp. 533-537. https://doi.org/10.1016/S1005-8850(07)60123-6
Cite this article as:
Zhenhua Li and Xianhua Cheng, Deformation temperature and postdeformation annealing effects on severely deformed TiNi alloy by equal channel angular extrusion, J. Univ. Sci. Technol. Beijing, 14(2007), No. 6, pp. 533-537. https://doi.org/10.1016/S1005-8850(07)60123-6
Materials

Deformation temperature and postdeformation annealing effects on severely deformed TiNi alloy by equal channel angular extrusion

+ Author Affiliations
  • Corresponding author:

    Xianhua Cheng    E-mail: xhcheng@sjtu.edu.cn

  • Received: 9 December 2006
  • Micron TiNi alloy blocks were fabricated at high temperature by equal channel angular extrusion (ECAE) using hotforged Ti-50.3at%Ni alloy as the raw material and the effects of deformation temperature and postdeformation annealing on the severely deformed TiNi alloy by ECAE were investigated. The results show that the TiNi alloy processed by ECAE undergoes severe plastic deformation, and lowering the deformation temperature and increasing the number of extrusions contribute to grain refinement. When the annealing temperature is below 873 K, static recovery is the main restoration process; when the temperature rises to 973 K, static recrystallization occurs. It is found that fine particles are precipitated when the TiNi alloy processed by ECAE is annealed at 773 K.
  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Share Article

    Article Metrics

    Article Views(240) PDF Downloads(7) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return